journal article·2023-08-23

Low Interfacial Resistance and Superior Suppression to Li-Dendrite Penetration Facilitated by Air-Stable and Mechanically Robust Al/Mg-Co-Doped Li-La-Zirconate as Electrolyte for Li-Based Solid-State Cells

Sushobhan Kobi, Ankur Sharma, Amartya Mukhopadhyay

ACS Applied Materials & Interfaces· Volume 15· Issue 33
Publisher page

Abstract

In the context of usage as a solid electrolyte (SE) for Li-based solid-state cells, the interfacial characteristics of Li-La-zirconate (LLZO) with the electrodes and the mechanical properties of LLZO influence the overall impedance and stability. In this regard, the newly developed air-stable Al/Mg-co-doped LLZO has been found to possess greater resistance to crack propagation (by ∼31%) and fracture stress (by ∼52%), along with elevated hardness and stiffness, as compared to simply Al-doped LLZO. Furthermore, as directly visualized via cross-section electron microscopy at the Li/LLZO interfaces, the air-stability, along with mechanical robustness of Al/Mg-co-doped LLZO, facilitates the complete absence of impurity phase and cracks at the Li/LLZO interface, unlike for the simply Al-doped LLZO. These result in a very low area specific resistance for the Li/“Al/Mg-co-doped LLZO” interface of ∼9 Ω cm 2, which is ∼3 times lower than that at the Li/“Al-doped LLZO” interface and is also among the lowest reported to date for Li/LLZO interfaces, that too sans any surface/interfacial coating/engineering. Galvanostatic Li-plating/stripping cycles indicate that the critical current density toward initiating Li-dendrite nucleation/propagation is higher in the case of Al/Mg-co-doped LLZO SE, viz., ∼0.45 mA/cm 2, than for the Al-doped counterpart (viz., ∼0.25 mA/cm 2 ). Furthermore, Li-stripping/plating cycles @ 0.1 mA/cm 2 have revealed outstanding stability of polarization voltage up to at least 100 cycles upon using Al/Mg-codoped LLZO as the SE, in contrast to the instability right from the 36th cycle onward with the Al-doped LLZO. This indicates superior suppression toward Li-dendrite nucleation/propagation by the Al/Mg-codoped LLZO, unlike by Al-doped LLZO, as also directly visualized via cross-section electron microscopy post-cycling. The air-stability induced a clean Li/LLZO interface (viz., good contact), which, together with the mechanical robustness of Al/Mg-codoped LLZO, resulted in the very low interfacial resistance and excellent suppression toward Li-dendrite nucleation/propagation, leading to high CCD and very stable long-term Li-stripping/plating. Overall, in addition to highlighting the notable advantages offered by the Al/Mg-co-doped LLZO solid electrolyte, the insights obtained as part of this work are expected to lead to the successful and facile development of high-performance solid-state Li-based cells.
Source: openalex_inverted_index · Quality: baseline

Research context

OpenAlex topics: Advanced Battery Materials and Technologies · Advancements in Battery Materials · Advanced Battery Technologies Research

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

Advanced Batteries and Ceramics Laboratory, Department of Metallurgical Engineering and Materials Science, Indian Institute of Technology Bombay, Mumbai 400076, India

Funding

Industrial Research and Consultancy Centre

References (64)

Show source-provided references
1. 10.1016/j.actamat.2012.10.03410.1016/j.actamat.2012.10.034 ↗
2. 10.1002/anie.20070114410.1002/anie.200701144 ↗
3. 10.1021/acsami.6b1390210.1021/acsami.6b13902 ↗
4. 10.1111/jace.1384410.1111/jace.13844 ↗
5. 10.1038/nmat482110.1038/nmat4821 ↗
6. 10.1021/acs.chemmater.7b0300210.1021/acs.chemmater.7b03002 ↗
7. 10.1149/2.0841704jes10.1149/2.0841704jes ↗
8. 10.1021/acsami.8b1835610.1021/acsami.8b18356 ↗
9. 10.1021/acsenergylett.9b0240110.1021/acsenergylett.9b02401 ↗
10. 10.1021/acs.chemmater.5b0385410.1021/acs.chemmater.5b03854 ↗
11. 10.1016/j.jpowsour.2017.01.03710.1016/j.jpowsour.2017.01.037 ↗
12. 10.1007/s11581-017-2314-410.1007/s11581-017-2314-4 ↗
13. 10.1016/j.jeurceramsoc.2018.06.01410.1016/j.jeurceramsoc.2018.06.014 ↗
14. 10.1016/j.scriptamat.2018.11.02610.1016/j.scriptamat.2018.11.026 ↗
15. 10.1149/1945-7111/abad6610.1149/1945-7111/abad66 ↗
16. 10.1016/j.jpowsour.2018.04.01610.1016/j.jpowsour.2018.04.016 ↗
17. 10.1021/acsami.7b0061410.1021/acsami.7b00614 ↗
18. 10.1038/nnano.2017.1610.1038/nnano.2017.16 ↗
19. 10.1038/s41563-019-0438-910.1038/s41563-019-0438-9 ↗
20. 10.1038/s41467-020-20463-y10.1038/s41467-020-20463-y ↗
21. 10.1021/jacs.6b0534110.1021/jacs.6b05341 ↗
22. 10.1126/sciadv.160165910.1126/sciadv.1601659 ↗
23. 10.1002/anie.20170863710.1002/anie.201708637 ↗
24. 10.1126/sciadv.abq015310.1126/sciadv.abq0153 ↗
25. 10.1039/C8TA02276C10.1039/C8TA02276C ↗
26. 10.1021/acs.nanolett.6b0469510.1021/acs.nanolett.6b04695 ↗
27. 10.1016/j.jpowsour.2019.22669110.1016/j.jpowsour.2019.226691 ↗
28. 10.1039/C9TA01911A10.1039/C9TA01911A ↗
29. 10.1021/acs.nanolett.8b0390210.1021/acs.nanolett.8b03902 ↗
30. 10.1021/acsenergylett.8b0045310.1021/acsenergylett.8b00453 ↗
31. 10.1016/j.jpowsour.2015.10.05310.1016/j.jpowsour.2015.10.053 ↗
32. 10.1007/s11581-021-04300-w10.1007/s11581-021-04300-w ↗
33. 10.1038/s41560-017-0047-210.1038/s41560-017-0047-2 ↗
34. 10.1149/1.185085410.1149/1.1850854 ↗
35. 10.1149/1.171089310.1149/1.1710893 ↗
36. 10.1007/BF0111736510.1007/BF01117365 ↗
37. 10.1557/JMR.1992.156410.1557/JMR.1992.1564 ↗
38. 10.1007/s10853-012-6687-510.1007/s10853-012-6687-5 ↗
39. 10.1111/j.1151-2916.1981.tb10320.x10.1111/j.1151-2916.1981.tb10320.x ↗
40. 10.1111/jace.1408410.1111/jace.14084 ↗
41. 10.1021/acsami.0c0168110.1021/acsami.0c01681 ↗
42. 10.1016/j.jeurceramsoc.2018.02.03210.1016/j.jeurceramsoc.2018.02.032 ↗
43. 10.1039/C7TA06790A10.1039/C7TA06790A ↗
44. 10.1111/j.1744-7402.2006.02068.x10.1111/j.1744-7402.2006.02068.x ↗
45. 10.1002/aenm.20170100310.1002/aenm.201701003 ↗
46. 10.1149/2.1391814jes10.1149/2.1391814jes ↗
47. 10.1039/C8SE00234G10.1039/C8SE00234G ↗
48. 10.1016/j.jpowsour.2012.01.09410.1016/j.jpowsour.2012.01.094 ↗
49. 10.1002/aenm.20220193910.1002/aenm.202201939 ↗
50. 10.1039/C3TA13999A10.1039/C3TA13999A ↗
51. 10.1002/adfm.20040004410.1002/adfm.200400044 ↗
52. 10.1039/C7TA03162A10.1039/C7TA03162A ↗
53. 10.1149/2.0721508jes10.1149/2.0721508jes ↗
54. 10.1038/nenergy.2016.3010.1038/nenergy.2016.30 ↗
55. 10.1016/j.mattod.2018.04.00410.1016/j.mattod.2018.04.004 ↗
56. 10.1149/2.086202jes10.1149/2.086202jes ↗
57. 10.1016/j.jpowsour.2017.11.08210.1016/j.jpowsour.2017.11.082 ↗
58. 10.1039/C8TA08366E10.1039/C8TA08366E ↗
59. 10.1021/am508111r10.1021/am508111r ↗
60. 10.1016/j.electacta.2016.12.01810.1016/j.electacta.2016.12.018 ↗
61. 10.1016/j.ssi.2014.11.01010.1016/j.ssi.2014.11.010 ↗
62. 10.1021/cm300964k10.1021/cm300964k ↗
63. 10.1021/acs.chemmater.5b0102310.1021/acs.chemmater.5b01023 ↗
64. 10.1016/j.ssi.2016.12.00510.1016/j.ssi.2016.12.005 ↗