Copper Substitution in P2-Type Sodium Layered Oxide To Mitigate Phase Transition and Enhance Cyclability of Sodium-Ion Batteries

Development of high-performance cathode materials is one of the key challenges in the practical application of sodium-ion batteries. Among all the cathode materials, layered sodium transition-metal oxides are particularly attractive. However, undesired phase transitions are often reported and have detrimental effects on the structure stability and electrochemical performance. Cu substitution of zinc in the P2-type Na0.6Mn0.7Ni0.15Zn0.15–xCuxO2 (x = 0, 0.075, and 0.15) composites was investigated in this study for mitigating the biphase transition and enhancing the electrochemical performance of sodium-ion batteries. The coupling effect of Zn and Cu enables an excellent capacity retention of 96.4% of the initial discharge capacity after 150 cycles at 0.1 C in the Na/Na0.6Mn0.7Ni0.15Zn0.075Cu0.075O2 cell. The biphase transition that occurred in the high voltage range has been significantly suppressed after the incorporation of Cu in Na0.6Mn0.7Ni0.15Zn0.15O2, which was confirmed by in situ X-ray diffraction studies. Moreover, the substitution of the inert element Zn with electrochemically active Cu leads to the suppression of anionic redox and the occurrence of Cu2+/3+ redox reaction, and the electrolyte decomposition is impeded after the introduction of electrochemically active Cu in the Na0.6Mn0.7Ni0.15Zn0.15–xCuxO2 composite cathode. The enhanced electrochemical performance in the Na0.6Mn0.7Ni0.15Zn0.075Cu0.075O2 electrode can be ascribed to the coexistence of Zn and Cu and alleviated volumetric change as well as suppressed electrode/electrolyte side reaction after Cu substitution.