Hierarchical Artificial Compound Eyes with Wide Field-of-View and Antireflection Properties Prepared by Nanotip-Focused Electrohydrodynamic Jet Printing

Artificial compound eyes (ACEs) endowed with durable superhydrophobicity, wide field-of-view (FOV), and antireflection properties are extremely appealing in advanced micro-optical systems. However, the simple and high-efficiency fabrication of ACEs with these functions is still a major challenge. Herein, inspired by moth eyes, ACEs with hierarchical macro/micro/nano structures were fabricated using the combination of nanotip-focused electrohydrodynamic jet (NFEJ) printing and air-assisted deformation processes. The NFEJ printing enables the direct and maskless fabrication of hierarchical micro/nanolens arrays (M/NLAs) without intermediate steps. The introduction of M/NLAs on the eye surface significantly improves the water hydrophobic performance with a water contact angle of 161.1° and contact angle hysteresis (CAH) of 4.2° and generally decreases the reflectance by 51% in the wavelength range of 350-1600 nm in comparison to the macroeye without any structures. The contact angle remains almost unchanged, and the CAH slightly increases from 4.2° to 8.7° after water jet impact for 20 min, indicating a durable superhydrophobicity. Moreover, the results confirm that the durable superhydrophobic ACEs with antireflection properties exhibit excellent imaging quality and a large FOV of up to 160° without distortion.