Highly Distorted Grain Boundary with an Enhanced Carrier/Phonon Segregation Effect Facilitates High-Performance Thermoelectric Materials
Source abstract
Abstract
Grain boundary plays an important role in determining the phonon/carrier transport behaviors of thermoelectric (TE) materials, especially for the polycrystalline materials with the average grain size in nanoscale dimensions. Adjusting the grain size and boundaries of TE materials is considered as an effective approach to decouple TE parameters and thereby synergistically optimize the TE performance. Here, the highly distorted grain boundary with an enhanced carrier/phonon segregation effect is introduced to the commercial n-type Bi2Te2.7Se0.3 matrix. The existence of highly distorted grain boundaries can not only enhance the interfacial Seebeck coefficient without significant detriment to the electrical conductivity but also increase the interfacial thermal resistance of grain boundaries, leading to the synergistic reduction of the thermal conductivity. As a result, a peak figure of merit zTmax ≈ 1.22@425 K and an average zTavg ≈ 1.1(300–500 K) are obtained, which are about 55 and 57% higher than the corresponding values of the commercial Bi2Te2.7Se0.3 matrix, respectively. This work represents a new avenue for improving the commercial Bi2Te2.7Se0.3 TE material, which could further promote the development of the TE technology.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Advanced Thermoelectric Materials and Devices · Thermal properties of materials · Thermal Radiation and Cooling Technologies
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
School of Advanced Materials, Peking University Shenzhen Graduate School, Shenzhen 518055, China
School of Materials Science and Engineering, Shanghai University, Shanghai 200444, China
Funding
National Natural Science Foundation of China · Guangdong Province
References (39)
Show source-provided references
1. 10.1002/aenm.20190415910.1002/aenm.201904159 ↗
2. 10.1002/adfm.20190150510.1002/adfm.201901505 ↗
3. 10.1126/science.115644610.1126/science.1156446 ↗
4. 10.1002/adfm.20190604110.1002/adfm.201906041 ↗
5. 10.1039/c9nr07591g10.1039/c9nr07591g ↗
6. 10.1002/admt.20180055610.1002/admt.201800556 ↗
7. 10.1021/ar400290f10.1021/ar400290f ↗
8. 10.1039/d1ta01016f10.1039/d1ta01016f ↗
9. 10.1039/c7ee03326e10.1039/c7ee03326e ↗
10. 10.1063/1.32633410.1063/1.326334 ↗
11. 10.1063/1.33379310.1063/1.333793 ↗
12. 10.1103/physrevb.103.10430110.1103/physrevb.103.104301 ↗
13. 10.1021/acsami.9b1678110.1021/acsami.9b16781 ↗
14. 10.1021/acsami.9b1939810.1021/acsami.9b19398 ↗
15. 10.1002/aenm.20150041110.1002/aenm.201500411 ↗
16. 10.1016/j.isci.2020.10134010.1016/j.isci.2020.101340 ↗
17. 10.1002/anie.20161204110.1002/anie.201612041 ↗
18. 10.1002/aelm.20200029210.1002/aelm.202000292 ↗
19. 10.1016/j.nanoen.2017.07.01110.1016/j.nanoen.2017.07.011 ↗
20. 10.1016/j.nanoen.2016.09.01810.1016/j.nanoen.2016.09.018 ↗
21. 10.1039/c7ee02007d10.1039/c7ee02007d ↗
22. 10.1002/aenm.20207017110.1002/aenm.202070171 ↗
23. 10.1039/d0ee01349h10.1039/d0ee01349h ↗
24. 10.1021/acsami.1c0241710.1021/acsami.1c02417 ↗
25. 10.1016/j.nanoen.2018.03.00910.1016/j.nanoen.2018.03.009 ↗
26. 10.1039/c9ta05798f10.1039/c9ta05798f ↗
27. 10.1039/c9nr07406f10.1039/c9nr07406f ↗
28. 10.1103/physrevb.57.1495810.1103/physrevb.57.14958 ↗
29. 10.1039/c9ee03921j10.1039/c9ee03921j ↗
30. 10.1016/j.actamat.2013.07.03710.1016/j.actamat.2013.07.037 ↗
31. 10.1063/1.34983010.1063/1.349830 ↗
32. 10.1063/1.36520910.1063/1.365209 ↗
33. 10.1039/d0ee02490b10.1039/d0ee02490b ↗
34. 10.1039/c7ee03326e10.1039/c7ee03326e ↗
35. 10.1063/1.34983010.1063/1.349830 ↗
36. 10.1111/j.1151-2916.1990.tb07576.x10.1111/j.1151-2916.1990.tb07576.x ↗
37. 10.1039/c8ee03225d10.1039/c8ee03225d ↗
38. 10.1002/anie.20150838110.1002/anie.201508381 ↗
39. 10.1039/c5mh00299k10.1039/c5mh00299k ↗