Different Response Kinetics to Temperature and Water Vapor of Acrylamide Polymers Obtained by Initiated Chemical Vapor Deposition

Paul Salzmann, Alberto Perrotta, Anna Maria Coclite

Abstract

Thermoresponsive polymers undergo a reversible phase transition at their lower critical solution temperature (LCST) from a hydrated hydrophilic state at temperatures below the LCST to a collapsed hydrophobic state at higher temperatures. This results in a strong response to temperature when in aqueous environment. This study shows that hydrogel thin films synthesized by initiated chemical vapor deposition show fast and strong response to temperature also in water vapor environment. Thin films of cross-linked poly(N-isopropylacrylamide), p(NIPAAm), were found to have a sharp change in thickness by 200% in water vapor at temperatures above and below the LCST. Additionally, the stimuli-responsive poly(N,N-diethylacrylamide) was investigated and compared to results found for p(NIPAAm). Analysis of the swelling kinetics performed with in situ spectroscopic ellipsometry with variable stage temperature shows differences for swelling and deswelling processes, and a hysteresis in the thickness profile was found as a function of temperature and of temperature change rate.
Source: openalex_inverted_index · Quality: baseline

Research context

OpenAlex topics: Hydrogels: synthesis, properties, applications · Advanced Sensor and Energy Harvesting Materials · Advanced Materials and Mechanics

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

Institute of Solid State Physics, Graz University of Technology, Petersgasse 16, 8010 Graz, Austria

Funding

European Commission

References (29)

Show source-provided references
1. 10.1142/s0219581x1100788010.1142/s0219581x11007880 ↗
2. 10.1038/nmat456910.1038/nmat4569 ↗
3. 10.1021/acsami.5b0018110.1021/acsami.5b00181 ↗
4. Chu L.-Y. · 201310.1007/978-3-642-39538-3 ↗
5. 10.1016/j.addr.2012.11.00410.1016/j.addr.2012.11.004 ↗
6. 10.1016/j.jmps.2007.05.01410.1016/j.jmps.2007.05.014 ↗
7. 10.1002/marc.20100045210.1002/marc.201000452 ↗
8. 10.1021/j100373a08810.1021/j100373a088 ↗
9. 10.1021/acs.chemmater.6b0023010.1021/acs.chemmater.6b00230 ↗
10. 10.1063/1.45511510.1063/1.455115 ↗
11. 10.1016/s0168-3659(97)00151-x10.1016/s0168-3659(97)00151-x ↗
12. 10.1021/ja010609f10.1021/ja010609f ↗
13. 10.1002/masy.1996109010510.1002/masy.19961090105 ↗
14. 10.1002/app.1994.07052011010.1002/app.1994.070520110 ↗
15. 10.1021/bm060607t10.1021/bm060607t ↗
16. 10.1021/ma101983s10.1021/ma101983s ↗
17. 10.1021/la201935r10.1021/la201935r ↗
18. 10.1021/ma060161910.1021/ma0601619 ↗
19. 10.1021/acsami.7b0152710.1021/acsami.7b01527 ↗
20. 10.1016/j.polymer.2011.07.05110.1016/j.polymer.2011.07.051 ↗
21. 10.1021/la500359410.1021/la5003594 ↗
22. 10.1002/admi.20147002510.1002/admi.201470025 ↗
23. Gleason K. K. · 201510.1002/9783527690275 ↗
24. 10.1016/j.tsf.2011.01.28610.1016/j.tsf.2011.01.286 ↗
25. 10.1021/la034653f10.1021/la034653f ↗
26. 10.1016/s0927-7765(00)00155-710.1016/s0927-7765(00)00155-7 ↗
27. 10.1002/macp.20160027110.1002/macp.201600271 ↗
28. 10.1021/ma971873p10.1021/ma971873p ↗
29. 10.1021/ma052561m10.1021/ma052561m ↗