Enhanced Thermoelectric Performance in n-Type SrTiO₃/SiGe Composite

Silicon germanium (SiGe) alloys hold promise for thermoelectric power generation at high temperatures and have been applied in deep-space missions. However, enhancement of the dimensionless thermoelectric figure-of-merit (ZT) is still needed for practical civil applications of SiGe. In this work, we report high-performance oxide/SiGe bulk composites that were obtained via hot-press sintering of mixed powders composed of phosphorus (P)-doped SiGe prepared via mechanical alloying, using a ball-milling technique and La–Nb-doped SrTiO3 (La–Nb–STO). The La–Nb–STO powder was obtained from ball milling of a bulk La–Nb–STO sample that was sintered via hot pressing of hydrothermally synthesized La–Nb–STO powder. Controlling the amount of La–Nb–STO nanoparticles added to SiGe matrix increased the power factor by optimizing the electron concentration and mobility in the composite. In addition, compared with single-phase P-doped SiGe, the second phase decreased the thermal conductivity because of additional phonon scattering at the interface. As a result, a high ZT of 0.91 was realized in the n-type oxide/SiGe bulk composite at 1000 K, which was 18% larger than that for the typical materials used in space flight missions and 5% higher than the single-phase SiGe alloys obtained in the present study. The strategy used in this study could also be viable to further enhance the ZT of nanostructured n-type SiGe and SrTiO3-based oxide materials.