Lithium Antievaporation-Loss Engineering via Sodium/Potassium Doping Enables Superior Electrochemical Performance of High-Nickel Li-Rich Layered Oxide Cathodes

Low-cost Mn- and Li-rich layered oxides suffer from rapid voltage decay, which can be improved by increasing the nickel content to derive high nickel Li-rich layered oxides (HNLO) but is normally accompanied by reduced capacity and inferior cycling stability. Herein, Na or K ions are successfully doped into the lattice of high nickel Li-rich Li1.2–xMxNi0.32Mn0.48O2 (M = Na, K) layered oxides via a facile expanded graphite template-sacrificed approach. Both Na- and K-doped samples exhibit excellent rate capability and cycling stability compared with the un-doped one. The Na-doped sample shows a capacity retention of 93% after 200 cycles at 1C, which is quite outstanding for HNLO. The greatly improved electrochemical performances are attributed to the increased effective Li content in the lattice via Li antievaporation-loss engineering, the expanded Li slab, the pillaring effect, the increased C2/m component, and the improved electronic conductivity. Different performances by the introduction of sodium and potassium ions may be ascribed to their different ionic radii, which give rise to their different doping behaviors and threshold doping amounts. This work provides a new idea of enhancing electrochemical performance of HNLO by doping proper alien elements to increase the lattice lithium content effectively.