Effect of Titanium Substitution in a P2-Na_2/3Co_0.95Ti_0.05O₂ Cathode Material on the Structural and Electrochemical Properties

Worries about lithium supplies have led to the development of research on sodium batteries. Sodium-ion batteries are regarded as the next generation of energy-storage devices thanks to the generous resources of sodium. In spite of that, structural changes in the electrode materials remain the main challenge of this storage technology. NaCoO 2 has been widely investigated as a competitive candidate for LiCoO 2 . It has been found that the electrochemical cycling curves of this material present numerous potential steps as a result of electronic transitions and/or structural ordering. From this standpoint, this paper reports a novel cathode material, Na 2/3 Co 0.95 Ti 0.05 O 2, where 5% of cobalt was replaced by titanium, prepared via a facile solid-state route. The sodiation/desodiation mechanism of this layered material was investigated. Na//Na 2/3 Co 0.95 Ti 0.05 O 2 exhibits a first initial capacity of 119 mAh/g in the potential window 2–4.2 V with less potential jumps in the potential versus capacity curve compared to NaCoO 2 . Genuinely, the electrochemistry of this material demonstrated a reversibility upon the insertion/desinertion process with low polarization. In situ synchrotron investigations on Na 2/3 Co 0.95 Ti 0.05 O 2 reveal the occurrence of reversible ordered phases. Ex situ magic-angle-spinning NMR disclosed different environments around sodium starting from the pristine state to the end of charge.