H₂O–EG-Assisted Synthesis of Uniform Urchinlike Rutile TiO₂ with Superior Lithium Storage Properties

A facile green method to synthesize uniform nanostructured urchinlike rutile TiO2 is demonstrated. Titanium trichloride was selected as the TiO2 precursor, and a mixed solvent containing H2O and ethylene glycol was used. By using this binary medium, the nucleation and crystal growth of rutile TiO2 can be regulated, giving rise to very uniform urchinlike structures with tailorable sizes. As confirmed by the SEM and TEM analysis, large particles with dense aggregation of needle-like building blocks or small ones with loosely packed subunits could be obtained at different reaction conditions. The as-prepared samples were applied as the anode material for lithium-ion batteries, and they were shown to have superior properties with a high reversible capacity of 140 mA h g(-1) at a high current rate of 10 C for up to 300 cycles, which is almost unmatched by other rutile TiO2-based electrodes. A stable capacity of 88 mA h g(-1) can also be delivered at an extremely high rate of 50 C, suggesting the great potential of the as-prepared product for high-rate lithium-ion batteries.