Enhanced Lithiation Cycle Stability of ALD-Coated Confined a-Si Microstructures Determined Using In Situ AFM
Source abstract
Abstract
Microfabricated amorphous silicon (a-Si) pits ∼4 μm in diameter and 100 nm thick were fabricated to be partially confined in a nickel (Ni) current collector. Corresponding unconfined pillars were also fabricated. The samples were coated with 1.5, 3, or 6 nm of Al2O3 ALD. These samples were tested in electrolytes of 3:7 by weight ethylene carbonate:ethyl methyl carbonate (EC:EMC) with 1.2 M LiPF6 salt with and without 2% fluoroethylene carbonate (FEC) and in a pure FEC electrolyte with 10 wt % LiPF6. The samples were imaged with an atomic force microscope during electrochemical cycling to evaluate morphology evolution and solid electrolyte interphase (SEI) formation. The partially confined a-Si structures had superior cycle efficiency relative to the unconfined a-Si pillars. Additionally, samples with 3 nm of ALD achieved higher charge capacity and enhanced cycle life compared to samples without ALD, demonstrated thinner SEI formation, and after 10 cycles at a 1 C rate remained mostly intact and had actually decreased in diameter. Finally, the samples with 3 nm of ALD had better capacity retention in the baseline 3:7 EC:EMC than in either of the FEC containing electrolytes.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Advancements in Battery Materials · Semiconductor materials and interfaces · Supercapacitor Materials and Fabrication
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Electrochemistry Branch, US Army Research Laboratory, 2800 Powder Mill Road, Adelphi, Maryland 20783, United States
Electronic Science & Technology Division, US Naval Research Laboratory, Washington, DC 20375, United States
Chemistry Division, US Naval Research Laboratory, Washington, DC 20375, United States
Funding
U.S. Army Research Laboratory · Nanoscience Institute - U.S. Naval Research Laboratory
References (37)
Show source-provided references
1. 10.1038/3510464410.1038/35104644 ↗
2. 10.1149/1.155659510.1149/1.1556595 ↗
3. 10.1038/nnano.2007.41110.1038/nnano.2007.411 ↗
4. 10.1149/1.138817810.1149/1.1388178 ↗
5. 10.1016/j.jpowsour.2006.09.08410.1016/j.jpowsour.2006.09.084 ↗
6. 10.1149/1.305598410.1149/1.3055984 ↗
7. 10.1149/1.169741210.1149/1.1697412 ↗
8. 10.1016/j.coche.2013.07.00110.1016/j.coche.2013.07.001 ↗
9. 10.1016/j.jpowsour.2007.06.14910.1016/j.jpowsour.2007.06.149 ↗
10. 10.1149/2.076205jes10.1149/2.076205jes ↗
11. 10.1021/ja103199710.1021/ja1031997 ↗
12. 10.1021/acs.nanolett.5b0304710.1021/acs.nanolett.5b03047 ↗
13. 10.1021/acsnano.5b0168110.1021/acsnano.5b01681 ↗
14. 10.1016/j.mattod.2014.04.02610.1016/j.mattod.2014.04.026 ↗
15. 10.1016/j.powtec.2005.04.00910.1016/j.powtec.2005.04.009 ↗
16. 10.1039/C4NR01954G10.1039/C4NR01954G ↗
17. 10.1016/j.sna.2011.12.02910.1016/j.sna.2011.12.029 ↗
18. 10.1002/maco.20140801210.1002/maco.201408012 ↗
19. 10.1007/s11837-009-0081-z10.1007/s11837-009-0081-z ↗
20. 10.1021/nl301495610.1021/nl3014956 ↗
21. 10.1002/adma.20130471410.1002/adma.201304714 ↗
22. 10.1016/j.jpowsour.2014.10.20710.1016/j.jpowsour.2014.10.207 ↗
23. 10.1039/C5EE01254F10.1039/C5EE01254F ↗
24. 10.1021/jz401825510.1021/jz4018255 ↗
25. 10.1002/adma.20110256810.1002/adma.201102568 ↗
26. 10.1002/adma.20110191510.1002/adma.201101915 ↗
27. 10.1021/acsami.5b0185310.1021/acsami.5b01853 ↗
28. 10.1021/nn505523c10.1021/nn505523c ↗
29. 10.1021/nl202088h10.1021/nl202088h ↗
30. 10.1021/nn403790910.1021/nn4037909 ↗
31. 10.1016/j.jpowsour.2014.01.07710.1016/j.jpowsour.2014.01.077 ↗
32. 10.1021/am500363t10.1021/am500363t ↗
33. 10.1149/1.173921710.1149/1.1739217 ↗
34. 10.1021/nl304450810.1021/nl3044508 ↗
35. 10.2478/s11534-011-0096-210.2478/s11534-011-0096-2 ↗
36. 10.1149/2.0081506jes10.1149/2.0081506jes ↗
37. 10.1149/2.001404jes10.1149/2.001404jes ↗