Improved Adhesion of Dense Silica Coatings on Polymers by Atmospheric Plasma Pretreatment

Oxygen atmospheric plasma was used to pretreat polycarbonate (PC) and stretched poly(methyl methacrylate) (PMMA) surfaces in order to enhance the adhesion of the dense silica coatings deposited by atmospheric plasma on the polymer substrates. The treatment time and chemical structure of the polymers were found to be important factors. For PC, a short treatment increased the adhesion energy, while longer treatment times decreased the adhesion. In contrast, plasma pretreatment monotonically decreased the adhesion of PMMA, and pristine PMMA exhibited much higher adhesion than the PC counterpart. We found that adhesion enhancement was achieved through improved chemical bonding, chain interdiffusion, and mechanical interlocking at the coating/substrate interface, after a short atmospheric plasma treatment. Decreased adhesion resulted from overoxidation and low-molecular-weight weak layer formation on the polymer surface by prolonged atmospheric plasma treatment. The dramatic differences in the behavior of PC and PMMA in relation to the plasma treatment time were due to their dissimilar resistance to atmospheric plasma exposure.