Cross-Linkable Fluorene-Diphenylamine Derivatives for Electrochromic Applications

Multicolor electrochromic systems based on heat cross-linkable arylamine-substituted fluorene derivatives, FD and FDOMe, are reported. These derivatives with pendant vinyl groups have been synthesized by the Buchwald-Hartwig amination reaction and were well-characterized using various analytical and spectroscopic techniques such as NMR, ESI-MS, and single-crystal X-ray diffraction analysis. FD and FDOMe exhibited thermally activated cross-linking above their melting temperatures, which was confirmed through absorption, differential scanning calorimetry (DSC), FT-IR, and wide-angle X-ray diffraction (WAXD) techniques. Cross-linked FD films (FD-X) on ITO showed two reversible redox peaks at 0.74 and 0.91 V (versus Ag/AgCl) that correspond to the formation of radical cations and dications, respectively. The corresponding redox peaks were observed at 0.6 and 0.8 V for cross-linked FDOMe films (FDOMe-X). Spectroelectrochemical studies of the electrochromic films on ITO revealed multicolor electrochromism of FD-X (colorless-yellow-dark cyan) and FDOMe-X (colorless-brick red-blue) with a color contrast of ∼44% at 485 nm for FD-X and ∼63% at 500 nm for FDOMe-X and good switching stability between the neutral and oxidized states (>300 cycles) with low switching voltages (<0.9 V for the first oxidation and <1.3 V for the second oxidation). Furthermore, fabrication of electrochromic devices using FD-X and FDOMe-X on FTO substrate with PMMA-based solid electrolyte was demonstrated, where the devices exhibited reasonably low switching time between the redox states (<30 s) with good optical contrast.