Ultralong, Small-Diameter TiO2 Nanotubes Achieved by an Optimized Two-Step Anodization for Efficient Dye-Sensitized Solar Cells
Source abstract
Abstract
An optimized two-step anodization is developed to fabricate ultralong, small-diameter TiO2 nanotubes, that is, with tube length of up to 31 μm and pore diameter of about 35 nm in this work. This overcomes the length limitation of small diameter tubes that usually presents in conventional one-step anodization. The small tubes with lengths of 23 μm yield a conversion efficiency of 5.02% in dye-sensitized solar cells under nonoptimized conditions.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: TiO2 Photocatalysis and Solar Cells · Advanced Photocatalysis Techniques · Advanced Nanomaterials in Catalysis
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
School of Materials Science and Engineering, Chongqing University, Chongqing 400044, P. R. China
References (36)
Show source-provided references
1. Ariga K. · Bull. Chem. Soc. Jpn. · 2012 · 85 · 110.1246/bcsj.20110162 ↗
2. Chen H. · Chem. Soc. Rev. · 2013 · 42 · 267910.1039/C2CS35367A ↗
3. Kubacka A. · Chem. Rev. · 2012 · 112 · 155510.1021/cr100454n ↗
4. Zhang Q. · Nanosci. Nanotechnol. Lett. · 2012 · 4 · 50510.1166/nnl.2012.1345 ↗
5. Kummer K. M. · Nanosci. Nanotechnol. Lett. · 2012 · 4 · 48310.1166/nnl.2012.1352 ↗
6. O’Regan B. · Nature · 1991 · 353 · 73710.1038/353737a0 ↗
7. Grätzel M. · J. Photochem. Photobiol. C · 2003 · 4 · 14510.1016/S1389-5567(03)00026-1 ↗
8. Grätzel M. · Inorg. Chem. · 2005 · 44 · 684110.1021/ic0508371 ↗
9. Grätzel M. · J. Photochem. Photobiol. A · 2004 · 164 · 310.1016/j.jphotochem.2004.02.023 ↗
10. Nazeeruddin M. K. · J. Am. Chem. Soc. · 2005 · 127 · 1683510.1021/ja052467l ↗
11. Yella A. · Science · 2011 · 334 · 62910.1126/science.1209688 ↗
12. Mor G. K. · Nano Lett. · 2006 · 6 · 21510.1021/nl052099j ↗
13. Zhu K. · Nano Lett. · 2007 · 7 · 6910.1021/nl062000o ↗
14. Sun L. · Nanosci. Nanotechnol. Lett. · 2012 · 4 · 47110.1166/nnl.2012.1355 ↗
15. Roy P. · Electrochem. Commun. · 2009 · 11 · 100110.1016/j.elecom.2009.02.049 ↗
16. Kim D. · Electrochem. Commun. · 2010 · 12 · 57410.1016/j.elecom.2010.02.003 ↗
17. Sun L. · ChemPhysChem · 2011 · 12 · 363410.1002/cphc.201100450 ↗
18. Ye M. D. · Nano Lett. · 2011 · 11 · 321410.1021/nl2014845 ↗
19. Wang X. · RSC Adv. · 2013 · 3 · 1100110.1039/c3ra23482g ↗
20. Pan X. A. · Nanotechnology · 2011 · 22 · 1
21. Lin L.-Y. · J. Power Sources · 2013 · 243 · 53510.1016/j.jpowsour.2013.05.163 ↗
22. Ghicov A. · Chem. Asian J. · 2009 · 4 · 52010.1002/asia.200800441 ↗
23. Liu N. · Electrochem. Commun. · 2012 · 15 · 110.1016/j.elecom.2011.11.003 ↗
24. Roy P. · Nanoscale · 2010 · 2 · 4510.1039/B9NR00131J ↗
25. Bauer S. · Electrochem. Commun. · 2006 · 8 · 132110.1016/j.elecom.2006.05.030 ↗
26. Yasuda K. · Electrochim. Acta · 2007 · 52 · 405310.1016/j.electacta.2006.11.023 ↗
27. Sun L. · J. Electroanal. Chem. · 2009 · 637 · 610.1016/j.jelechem.2009.09.023 ↗
28. Prakasam H. E. · J. Phys. Chem. C · 2007 · 111 · 723510.1021/jp070273h ↗
29. Liu X. · RSC Adv. · 2013 · 3 · 488510.1039/c3ra40221e ↗
30. Sun L. · Energy Environ. Sci. · 2011 · 4 · 224010.1039/c1ee01196k ↗
31. Sun L. · J. Nanosci. Nanotechnol. · 2010 · 10 · 455110.1166/jnn.2010.1695 ↗
32. Wang X. · Thin Solid Films · 2011 · 519 · 469410.1016/j.tsf.2011.01.016 ↗
33. Wang X. · Electrochim. Acta · 2013 · 107 · 20010.1016/j.electacta.2013.06.047 ↗
34. Chen B. · Langmuir · 2012 · 28 · 293710.1021/la204154h ↗
35. Macak J. M. · Angew. Chem., Int. Ed. · 2005 · 44 · 746310.1002/anie.200502781 ↗
36. Varghese O. K. · Nat. Nanotechnol. · 2009 · 4 · 59210.1038/nnano.2009.226 ↗