Direct Assembly of 3D-BCN Microspheres as a Microsupercapacitor Electrode for Wearable Energy Storage

Scalable and cost-effective fabrication of three-dimensional (3D) boron carbon nitride (BCN) microspheres was first demonstrated by hydrothermal and annealing methods. In particular, the specific surface area of 3D-BCN-4 reached 1390.12 m2 g–1 and had a high hierarchical pore structure. An all-printed solid-state flexible microsupercapacitor (MSC) based on 3D-BCN-4 microspheres as an electrode material was fabricated for the first time by a screen printing method, which also provided efficacious properties. The single MSC areal capacitance reached 41.6 mF cm–2. Furthermore, the remarkable mechanical flexibility was also achieved for the device with evidence that no obvious capacitance loss occurred even upon bending to 180°, and the device had a 93.3% capacitance retention after 1000 cycles. In addition, the maximum energy density reached 0.00832 mW h cm–2, and the highest power density was 2 mW cm–2. These results show the synthesis of 3D-BCN by a facile and effective method with excellent electrochemical performance, which should provide a promising direction to wearable energy storage devices.