Efficient Technologies for the Fabrication of Dense TaB2-Based Ultra-High-Temperature Ceramics

Roberta Licheri, Roberto Orrù, Clara Musa, Giacomo Cao

Publisher page

Abstract

A 20 min ball-milling treatment (ball to powders ratio equal to 1) was demonstrated to be a valuable method for mechanochemically activating Ta, B 4 C, Si, and graphite to prepare TaB 2 −SiC and TaB 2 −TaC−SiC ultrarefractory composites by self-propagating high-temperature synthesis (SHS). The resulting completely converted powders were spark plasma sintered at 1800 °C for 30 min, thus obtaining products about 96% dense. TGA characterization of bulk materials confirmed the beneficial effect of SiC in the resistance to oxidation behavior of the composite materials, while the presence of TaC appears to be unfavorable from this point of view. The obtained mechanical properties are in general comparable to those ones of Ta-based monolithic and composite bulk ceramics densified in previous works, although fracture toughness is significantly higher for TaB 2 −SiC. This outcome holds also true when the comparison is extended to the TaB 2 −TaC−SiC sample sintered in this work. The possible explanation is based on the occurrence of several toughening mechanisms (crack bridging, crack deflection, frictional interlocking, and crack branching) involved when TaB 2 −SiC samples are subjected to the prescribed indentation conditions, whereas crack propagation is facilitated by the relatively finer and more homogeneous microstructure exhibited by the ternary system.
Source: openalex_inverted_index · Quality: baseline

Research context

OpenAlex topics: Advanced ceramic materials synthesis · Advanced materials and composites · MXene and MAX Phase Materials

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

Dipartimento di Ingegneria Chimica e Materiali, Unità di Ricerca del Consorzio Interuniversitario Nazionale per la Scienza e Tecnologia dei Materiali (INSTM), Unità di Ricerca del Consiglio Nazionale delle Ricerche (CNR), Dipartimento di Energia e Trasporti, Università degli Studi di Cagliari, Piazza D’Armi, 09123 Cagliari, Italy

References (23)

Show source-provided references
1. Upadhya K. · Am. Ceram. Soc. Bull. · 1997 · 76 · 51
2. Rapp R. · Mater. Today · 2006 · 9 · 610.1016/S1369-7021(06)71471-7 ↗
3. Fahrenholtz W. G. · J. Am. Ceram. Soc. · 2007 · 90 · 134710.1111/j.1551-2916.2007.01583.x ↗
4. Talmy I. G. · Electrochem. Soc. Proc. · 2001 · 12 · 144
5. Peng F. · J. Am. Ceram. Soc. · 2008 · 91 · 148910.1111/j.1551-2916.2008.02368.x ↗
6. Zhang X. · J. Am. Ceram. Soc. · 2008 · 91 · 412910.1111/j.1551-2916.2008.02780.x ↗
7. Peng F. · J. Mater. Res. · 2009 · 24 · 185510.1557/jmr.2009.0216 ↗
8. Zhang X. · Mater. Lett. · 2008 · 62 · 425110.1016/j.matlet.2008.06.052 ↗
9. Yeh C. L. · J. Alloys Compd. · 2009 · 478 · 16310.1016/j.jallcom.2008.11.081 ↗
10. Licheri R. · Ind. Eng. Chem. Res. · 2007 · 46 · 908710.1021/ie0701423 ↗
11. Licheri R. · Mater. Lett. · 2008 · 62 · 43210.1016/j.matlet.2007.05.066 ↗
12. Licheri R. · J. Alloys Compd. · 2009 · 478 · 57210.1016/j.jallcom.2008.11.092 ↗
13. Orrù R. · Mater. Sci. Eng., R · 2009 · 63 · 12710.1016/j.mser.2008.09.003 ↗
14. Cincotti A. · J. Chem. Technol. Biotechnol. · 2003 · 78 · 12210.1002/jctb.757 ↗
15. Matthews F. L. · 1994
16. Shetty D. K. · J. Mater. Sci. · 1985 · 20 · 187310.1007/BF00555296 ↗
17. Barin I. · 1989
18. Suryanarayana C. · Prog. Mater Sci. · 2001 · 46 · 110.1016/S0079-6425(99)00010-9 ↗
19. Tripp W. C. · Am. Ceram. Soc. Bull. · 1973 · 52 · 612
20. Hinze J. W. · J. Electrochem. Soc. · 1975 · 122 · 124910.1149/1.2134436 ↗
21. Monteverde F. · J. Eur. Ceram. Soc. · 2005 · 25 · 102510.1016/j.jeurceramsoc.2004.05.009 ↗
22. Zhang X. · J. Am. Ceram. Soc. · 2007 · 90 · 39310.1111/j.1551-2916.2006.01416.x ↗
23. Mishra S. K. · Mater. Sci. Eng., A · 2004 · 364 · 24910.1016/j.msea.2003.08.021 ↗