Palladium Nanoparticle Formation on TiO2(110) by Thermal Decomposition of Palladium(II) Hexafluoroacetylacetonate

Amir Gharachorlou, Michael D. Detwiler, Anna V. Nartova, Yu Lei, Junling Lu, Jeffrey W. Elam, W. Nicholas Delgass, Fabio H. Ribeiro, Dmitry Y. Zemlyanov

Publisher page

Abstract

Palladium nanoparticles were synthesized by thermal decomposition of palladium(II) hexafluoroacetylacetonate (Pd(hfac)2), an atomic layer deposition (ALD) precursor, on a TiO2(110) surface. According to X-ray photoelectron spectroscopy (XPS), Pd(hfac)2 adsorbs on TiO2(110) dissociatively yielding Pd(hfac)(ads), hfac(ads), and adsorbed fragments of the hfac ligand at 300 K. A (2 × 1) surface overlayer was observed by scanning tunneling microscopy (STM), indicating that hfac adsorbs in a bidentate bridging fashion across two Ti 5-fold atoms and Pd(hfac) adsorbs between two bridging oxygen atoms on the surface. Annealing of the Pd(hfac)(ads) and hfac(ads) species at 525 K decomposed the adsorbed hfac ligands, leaving PdO-like species and/or Pd atoms or clusters. Above 575 K, the XPS Pd 3d peaks shift toward lower binding energies and Pd nanoparticles are observed by STM. These observations point to the sintering of Pd atoms and clusters to Pd nanoparticles. The average height of the Pd nanoparticles was 1.2 ± 0.6 nm at 575 K and increased to 1.7 ± 0.5 nm following annealing at 875 K. The Pd coverage was estimated from XPS and STM data to be 0.05 and 0.03 monolayers (ML), respectively, after the first adsorption/decomposition cycle. The amount of palladium deposited on the TiO2(110) surface increased linearly with the number of adsorption/decomposition cycles with a growth rate of 0.05 ML or 0.6 Å per cycle. We suggest that the removal of the hfac ligand and fragments eliminates the nucleation inhibition of Pd nanoparticles previously observed for the Pd(hfac)2 precursor on TiO2.
Source: openalex_inverted_index · Quality: baseline

Research context

OpenAlex topics: Electronic and Structural Properties of Oxides · Catalytic Processes in Materials Science · Semiconductor materials and devices

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

School of Chemical Engineering, Purdue University, West Lafayette, Indiana 47907, United States

Boreskov Institute of Catalysis, Novosibirsk 630090, Russia

Novosibirsk State University, Novosibirsk 630090, Russia

Energy Systems Division, Argonne National Laboratory, Argonne, Illinois 60439, United States

Birck Nanotechnology Center, Purdue University, West Lafayette, Indiana 47907, United States

Funding

Basic Energy Sciences

References (42)

Show source-provided references
1. Biffis A. · J. Mol. Catal. A: Chem. · 2001 · 173 · 24910.1016/S1381-1169(01)00153-4 ↗
2. Molnár Á. · J. Mol. Catal. A: Chem. · 2001 · 173 · 18510.1016/S1381-1169(01)00150-9 ↗
3. Blaser H.-U. · J. Mol. Catal. A: Chem. · 2001 · 173 · 310.1016/S1381-1169(01)00143-1 ↗
4. Zhu G. · J. Phys. Chem. B · 2004 · 109 · 233110.1021/jp0488665 ↗
5. Gabasch H. · J. Catal. · 2006 · 242 · 34010.1016/j.jcat.2006.06.022 ↗
6. Newton M. A. · Nat. Mater. · 2007 · 6 · 52810.1038/nmat1924 ↗
7. Feng H. · Catal. Lett. · 2011 · 141 · 51210.1007/s10562-011-0548-8 ↗
8. Elam J. W. · Thin Solid Films · 2006 · 515 · 166410.1016/j.tsf.2006.05.049 ↗
9. Lu J. · Science · 2012 · 335 · 120510.1126/science.1212906 ↗
10. Feng H. · Chem. Mater. · 2010 · 22 · 313310.1021/cm100061n ↗
11. Lu J. · Chem. Mater. · 2012 · 24 · 204710.1021/cm300203s ↗
12. Feng H. · ACS Catal. · 2011 · 1 · 66510.1021/cs2000957 ↗
13. Rikkinen E. · J. Phys. Chem. C · 2011 · 115 · 2306710.1021/jp2083659 ↗
14. Hämäläinen J. · Chem. Mater. · 2013 · 26 · 78610.1021/cm402221y ↗
15. Goldstein D. N. · Thin Solid Films · 2011 · 519 · 533910.1016/j.tsf.2011.02.037 ↗
16. Lu J. · Langmuir · 2010 · 26 · 1648610.1021/la101378s ↗
17. Weber M. J. · J. Phys. Chem. C · 2014 · 118 · 870210.1021/jp5009412 ↗
18. Anderson V. R. · J. Phys. Chem. C · 2014 · 118 · 896010.1021/jp412539y ↗
19. Parmeter J. E. · J. Phys. Chem. · 1993 · 97 · 1153010.1021/j100146a030 ↗
20. Mulley J. S. · Surf. Sci. · 2008 · 602 · 296710.1016/j.susc.2008.07.026 ↗
21. Lei Y. · J. Phys. Chem. C · 2013 · 117 · 1114110.1021/jp401196f ↗
22. Zaera F. · J. Phys. Chem. Lett. · 2012 · 3 · 130110.1021/jz300125f ↗
23. Horcas I. · Rev. Sci. Instrum. · 2007 · 78 · 013705-110.1063/1.2432410 ↗
24. Diebold U. · Surf. Rev. Lett. · 2000 · 7 · 61310.1142/S0218625X0000052X ↗
25. Fadley C. S. · 1978 · 2 · 1
26. Scofield J. H. · J. Electron Spectrosc. Relat. Phenom. · 1976 · 8 · 12910.1016/0368-2048(76)80015-1 ↗
27. Yeh J. J. · At. Data Nucl. Data Tables · 1985 · 32 · 110.1016/0092-640X(85)90016-6 ↗
28. Powell, C. J.; Jablonski, A.NIST Electron Effective-Attenuation-Length Database- Version1.3;National Institute of Standards and Technology:Gaithersburg, MD, 2011.
29. Yu J. C. · Chem. Mater. · 2002 · 14 · 380810.1021/cm020027c ↗
30. Gabasch H. · Surf. Sci. · 2006 · 600 · 298010.1016/j.susc.2006.05.029 ↗
31. Lin W. B. · J. Am. Chem. Soc. · 1996 · 118 · 597710.1021/ja944130h ↗
32. Beamson G. · 1992
33. Cohen S. L. · Appl. Phys. Lett. · 1992 · 60 · 5010.1063/1.107370 ↗
34. Cohen S. L. · Appl. Phys. Lett. · 1992 · 60 · 158510.1063/1.107259 ↗
35. Donnelly V. M. · J. Vac. Sci. Technol., A · 1993 · 11 · 6610.1116/1.578721 ↗
36. Lin W. B. · J. Am. Chem. Soc. · 1996 · 118 · 598810.1021/ja944131+ ↗
37. Cheung T. T. P. · Surf. Sci. · 1983 · 127 · L129
38. Diebold U. · Surf. Sci. Rep. · 2003 · 48 · 5310.1016/S0167-5729(02)00100-0 ↗
39. Horton J. H. · Surf. Sci. · 1997 · 375 · 17110.1016/S0039-6028(96)01282-4 ↗
40. Rayner D. G. · J. Vac. Sci. Technol., A · 2012 · 31 · 01A121 1
41. Siedle A. R. · Inorg. Chem. · 1983 · 22 · 228110.1021/ic00158a012 ↗
42. Bennett R. A. · Catal. Lett. · 1999 · 59 · 9910.1023/A:1019053512230 ↗