Conversion of “Waste Plastic” into Photocatalytic Nanofoams for Environmental Remediation
Source abstract
Abstract
Plastic debris is a major environmental concern, and to find effective ways to reuse polystyrene (PS) presents major challenges. Here, it is demonstrated that polystyrene foams impregnated with SnO2 are easily generated from plastic debris and can be applied to photocatalytic degradation of dyes. SnO2 nanoparticles were synthesized by a polymeric precursor method, yielding specific surface areas of 15 m2/g after heat treatment to 700 °C. Crystallinity, size, and shape of the SnO2 particles were assessed by X-ray diffraction (XRD) and transmission electron microscopy (TEM), demonstrating the preparation of crystalline spherical nanoparticles with sizes around 20 nm. When incorporated into PS foams, which were generated using a thermally induced phase separation (TIPS) process, the specific surface area increased to 48 m2/g. These PS/SnO2 nanofoams showed very good efficiency for photodegradation of rhodamine B, under UV irradiation, achieving up to 98.2% removal. In addition the PS/SnO2 nanofoams are shown to retain photocatalytic activity for up to five reuse cycles.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: TiO2 Photocatalysis and Solar Cells · Advanced Photocatalysis Techniques · Nanomaterials for catalytic reactions
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Departamento de Química, Universidade Estadual da Paraíba, Campina Grande 58429-500, Brazil
Programa de Pós-Graduação em Ciência de Materiais, Universidade Federal de Pernambuco, Recife 50740-540, Brazil
Instituto de Química, Universidade de Brasília, Brasília 70297-400, Brazil
Departamento de Química Fundamental, Universidade Federal de Pernambuco, Recife 50740-540, Brazil
Centro de Tecnologias Estratégicas do Nordeste, Ministério da Ciência, Tecnologia, Inovações e Comunicações, Recife 50740-545, Brazil
School of Chemistry, University of Bristol, Bristol BS8 1TS, U.K.
Funding
Funda??o de Amparo ? Ci?ncia e Tecnologia do Estado de Pernambuco · Conselho Nacional de Desenvolvimento Cient?fico e Tecnol?gico · Financiadora de Estudos e Projetos · Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior · University of Bristol
References (55)
Show source-provided references
1. 10.1016/j.apcatb.2014.05.03510.1016/j.apcatb.2014.05.035 ↗
2. 10.1016/j.jenvman.2010.05.00310.1016/j.jenvman.2010.05.003 ↗
3. 10.1016/j.powtec.2011.09.01410.1016/j.powtec.2011.09.014 ↗
4. 10.1016/j.ceramint.2016.01.05410.1016/j.ceramint.2016.01.054 ↗
5. Saharan V. · 2015
6. 10.1016/j.spmi.2016.01.01410.1016/j.spmi.2016.01.014 ↗
7. 10.1080/0191951870855214810.1080/01919518708552148 ↗
8. 10.1039/c1ee02110a10.1039/c1ee02110a ↗
9. 10.1016/j.jphotochemrev.2007.12.00310.1016/j.jphotochemrev.2007.12.003 ↗
10. 10.1246/cl.2002.66010.1246/cl.2002.660 ↗
11. 10.1016/S0960-8524(00)00080-810.1016/S0960-8524(00)00080-8 ↗
12. 10.1016/j.egypro.2014.06.06810.1016/j.egypro.2014.06.068 ↗
13. 10.1016/j.spmi.2015.03.01710.1016/j.spmi.2015.03.017 ↗
14. 10.1016/j.pmatsci.2014.06.00310.1016/j.pmatsci.2014.06.003 ↗
15. 10.1016/j.apcatb.2015.12.05310.1016/j.apcatb.2015.12.053 ↗
16. 10.1016/j.ccr.2015.12.00510.1016/j.ccr.2015.12.005 ↗
17. 10.1016/j.solmat.2011.04.02210.1016/j.solmat.2011.04.022 ↗
18. 10.1016/0032-3861(85)90186-710.1016/0032-3861(85)90186-7 ↗
19. 10.1021/la00028a00610.1021/la00028a006 ↗
20. 10.1007/s10973-006-7778-910.1007/s10973-006-7778-9 ↗
21. 10.1002/jbm.a.3162110.1002/jbm.a.31621 ↗
22. 10.1016/j.materresbull.2012.09.00810.1016/j.materresbull.2012.09.008 ↗
23. Nireesha G. R. · Int. J. Nov. trends Pharm. Sci. · 2013 · 3 · 87
24. Alger M. · 201710.1007/978-94-024-0893-5 ↗
25. 10.1016/j.jhazmat.2011.03.01110.1016/j.jhazmat.2011.03.011 ↗
26. 10.1016/S1001-0742(13)60441-610.1016/S1001-0742(13)60441-6 ↗
27. 10.1016/j.physb.2009.10.05610.1016/j.physb.2009.10.056 ↗
28. 10.1016/j.apcatb.2006.06.02210.1016/j.apcatb.2006.06.022 ↗
29. 10.1590/S0100-4042201400010000410.1590/S0100-40422014000100004 ↗
30. 10.1016/j.ica.2010.03.02410.1016/j.ica.2010.03.024 ↗
31. 10.1016/j.mssp.2014.07.04810.1016/j.mssp.2014.07.048 ↗
32. 10.1016/j.apsusc.2015.04.19810.1016/j.apsusc.2015.04.198 ↗
33. 10.1590/0104-1428.179810.1590/0104-1428.1798 ↗
34. 10.1016/j.snb.2008.10.01510.1016/j.snb.2008.10.015 ↗
35. 10.7763/IJCEA.2010.V1.4110.7763/IJCEA.2010.V1.41 ↗
36. 10.1016/j.ceramint.2015.07.06810.1016/j.ceramint.2015.07.068 ↗
37. 10.1021/cm049047010.1021/cm0490470 ↗
38. 10.1103/PhysRevB.5.314410.1103/PhysRevB.5.3144 ↗
39. 10.1016/j.jhazmat.2011.03.01110.1016/j.jhazmat.2011.03.011 ↗
40. 10.1016/j.apsusc.2015.04.16610.1016/j.apsusc.2015.04.166 ↗
41. 10.1021/ic900598310.1021/ic9005983 ↗
42. 10.1016/S1010-6030(98)00375-X10.1016/S1010-6030(98)00375-X ↗
43. 10.1021/jp905173e10.1021/jp905173e ↗
44. 10.1590/S0100-4042201400010000410.1590/S0100-40422014000100004 ↗
45. 10.1016/j.jphotochem.2013.11.01310.1016/j.jphotochem.2013.11.013 ↗
46. 10.1016/S0928-4931(01)00338-110.1016/S0928-4931(01)00338-1 ↗
47. 10.1007/BF0291407310.1007/BF02914073 ↗
48. 10.1179/1433075X12Y.000000004310.1179/1433075X12Y.0000000043 ↗
49. 10.1021/j100534a01210.1021/j100534a012 ↗
50. 10.1039/c2nr12010k10.1039/c2nr12010k ↗
51. 10.1016/j.micromeso.2013.11.03010.1016/j.micromeso.2013.11.030 ↗
52. 10.1016/j.jphotochem.2013.03.01110.1016/j.jphotochem.2013.03.011 ↗
53. 10.1016/j.apcatb.2013.06.01410.1016/j.apcatb.2013.06.014 ↗
54. 10.1016/j.matlet.2016.11.06710.1016/j.matlet.2016.11.067 ↗
55. 10.1016/j.matlet.2013.10.11110.1016/j.matlet.2013.10.111 ↗