Development of Dye-Sensitized Solar Cells Composed of Liquid Crystal Embedded, Electrospun Poly(vinylidene fluoride-co-hexafluoropropylene) Nanofibers as Polymer Gel Electrolytes

In order to overcome the problems associated with the use of liquid electrolytes in dye-sensitized solar cells (DSSCs), a new system composed of liquid crystal embedded, polymer electrolytes has been developed. For this purpose, three types of DSSCs have been fabricated. The cells contain electrospun poly(vinylidene fluoride-co-hexafluoropropylene) (e-PVdF-co-HFP) polymer gel electrolyte, with and without doping with the liquid crystal E7 and with a liquid electrolyte. The morphologies of the newly prepared DSSCs were explored using field emission scanning electron microscopy (FE-SEM). Analysis of the FE-SEM images indicate that the DSSC composed of E7 embedded on e-PVdF-co-HFP polymer gel electrolyte has a greatly regular morphology with an average diameter. The ionic conductivity of E7 embedded on e-PVdF-co-HFP polymer gel electrolyte was found to be 2.9 × 10(-3) S/cm at room temperature, a value that is 37% higher than that of e-PVdF-co-HFP polymer gel electrolyte. The DCCS containing the E7 embedded, e-PVdF-co-HFP polymer gel electrolyte was observed to possess a much higher power conversion efficiency (PCE = 6.82%) than that of an e-PVdF-co-HFP nanofiber (6.35%). In addition, DSSCs parameters of the E7 embedded, e-PVdF-co-HFP polymer gel electrolyte (V(oc) = 0.72 V, J(sc) = 14.62 mA/cm(2), FF = 64.8%, and PCE = 6.82% at 1 sun intensity) are comparable to those of a liquid electrolyte (V(oc) = 0.75 V, J(sc) = 14.71 mA/cm(2), FF = 64.9%, and PCE = 7.17%, both at a 1 sun intensity).