Probing Thermally Induced Decomposition of Delithiated Li_1.2–xNi_0.15Mn_0.55Co_0.1O₂ by in Situ High-Energy X-ray Diffraction

Safety of lithium-ion batteries has been a major barrier to large-scale applications. For better understanding the failure mechanism of battery materials under thermal abuse, the decomposition of a delithiated high energy cathode material, Li1.2-xNi0.15Mn0.55Co0.1O2, in the stainless-steel high pressure capsules was investigated by in situ high energy X-ray diffraction. The data revealed that the thermally induced decomposition of the delithiated transition metal (TM) oxide was strongly influenced by the presence of electrolyte components. When there was no electrolyte, the layered structure for the delithiated TM oxide was changed to a disordered Li1-xM2O4-type spinel, which started at ca. 266 °C. The disordered Li1-xM2O4-type spinel was decomposed to a disordered M3O4-type spinel phase, which started at ca. 327 °C. In the presence of organic solvent, the layered structure was decomposed to a disordered M3O4-type spinel phase, and the onset temperature of the decomposition was ca. 216 °C. When the LiPF6 salt was also present, the onset temperature of the decomposition was changed to ca. 249 °C with the formation of MnF2 phase. The results suggest that a proper optimization of the electrolyte component, that is, the organic solvent and the lithium salt, can alter the decomposition pathway of delithiated cathodes, leading to improved safety of lithium-ion batteries.