Tuning the Morphology of Li₂O₂ by Noble and 3d metals: A Planar Model Electrode Study for Li–O₂ Battery

In this work, a planar model electrode method has been used to investigate the structure–activity relationship of multiple noble and 3d metal catalysts for the cathode reaction of Li–O 2 battery. The result shows that the battery performance (discharge/charge overpotential) strongly depends not only on the type of catalysts but also on the morphology of the discharge product (Li 2 O 2 ). Specifically, according to electrochemical characterization and scanning electron microscopy (SEM) observation, noble metals (Pd, Pt, Ru, Ir, and Au) show excellent battery performance (smaller discharge/charge overpotential), with wormlike Li 2 O 2 particles with size less than 200 nm on their surfaces. On the other hand, 3d metals (Fe, Co, Ni, and Mn) offered poor battery performance (larger discharge/charge overpotential), with much larger Li 2 O 2 particles (1 μm to a few microns) on their surfaces after discharging. Further research shows that a “volcano plot” is found by correlating the discharging/charging plateau voltage with the adsorption energy of LiO 2 on different metals. The metals with better battery performance and worm-like-shaped Li 2 O 2 are closer to the top of the “volcano”, indicating adsorption energy of LiO 2 is one of the key characters for the catalyst to reach a good performance for the oxygen electrode of Li–O 2 battery, and it has a strong influence on the morphology of the discharge product on the electrode surface.