Incorporation of copper–indium back-end layers in the solution-based Cu(In, Ga)Se2 films: enhancement of photovoltaic performance of fabricated solar cells
Source abstract
Abstract
Abstract The morphology and photovoltaic properties of the solution-based Cu(In, Ga)Se2 films are effectively improved via the incorporation of copper-indium back-end layers in the precursor films. The effects on the concentrations of bimetal-ions solutions to prepare copper-indium back-end layers are investigated in this study. The incorporation of copper-indium back-end layer in the precursor film enhances the internal diffusion between gallium-ions and indium-ions during selenization reaction. Hence, the porous structure in the back-contact region of prepared CIGS films becomes densified, and the bandgap distribution of films shows a gradient profile. The densified morphology and gradient bandgap reduce the carrier recombination and improve the carrier collection of solar cells. In contrast to the pristine precursor film, the precursor film with a copper-indium back-end layer increase the conversion efficiency of prepared solar cells from 8.34% to 11.13%. The enhancement of conversion efficiency is attributed to the improvement of short-circuit current density and fill factor from 25.70 mA cm−2 to 31.79 mA cm−2 and 57.65% to 65.70%, respectively. This study reveals that the photovoltaic properties of solution-based CIGS solar cells can be improved significantly via the incorporation of copper-indium back-end layers into the precursor films.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Chalcogenide Semiconductor Thin Films · Quantum Dots Synthesis And Properties · Copper-based nanomaterials and applications
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (35)
Show source-provided references
1. CIS and CIGS nanomaterials prepared by solvothermal method and their spectral properties10.1002/crat.201400214 ↗
2. Sol-gel assisted preparation and characterization of silver indium diselenide powders10.1016/j.jallcom.2011.06.069 ↗
3. Sonochemical synthesis of CuIn0.7Ga0.3Se2 nanoparticles for thin film photo absorber application10.1016/j.mssp.2018.03.001 ↗
4. CuIn1-xGaxSe2 growth process modifications: influences on microstructure, Na distribution, and device properties10.1016/j.solmat.2011.01.003 ↗
5. CIGS thin film and device performance produced through a variation Ga concentration during three-stage growth process10.1016/j.mssp.2018.07.020 ↗
6. The effect of Cu concentration in the photovoltaic efficiency of CIGS solar cells prepared by co-evaporation technique10.1016/j.vacuum.2016.07.008 ↗
7. Potassium-induced surface modification of Cu(In, Ga)Se2 thin films for high-efficiency solar cells10.1038/nmat3789 ↗
8. CIGS absorbers and processes10.1002/pip.969 ↗
9. Deposition and application of a Mo-N back contact diffusion barrier yielding a 12.0% efficiency solution-processed CIGS solar cell using an amine-thiol solvent system10.1039/C8TA12089G ↗
10. Controlling growth chemistry and morphology of single-bath electrodeposited Cu(In, Ga)Se2 thin films for photovoltaic application10.1149/1.2186764 ↗
11. One-pot electrodeposition, characterization and photoactivity of stoichiometric copper indium gallium diselenide (CIGS) thin films for solar cells10.1039/c0cp00586j ↗
12. Cu(In, Ga)Se2 thin film absorber layer by flash light post-treatment10.1016/j.vacuum.2018.04.021 ↗
13. Liquid assisted grain growth in solution processed Cu(In, Ga)(S, Se)210.1016/j.solmat.2019.02.020 ↗
14. Effect of e-beam evaporated elemental metal stack precursors on the property of Cu(InGa)Se2 thin films through two-step process10.1007/s10854-018-0108-8 ↗
15. Influence of selenization temperatures on the microstructures and photoelectric properties of iron-ion doped Cu(In, Ga)Se2 thin-film solar cells10.1016/j.vacuum.2018.07.023 ↗
16. Synthesis of CuIn(S, Se)2 quaternary alloys by screen printing and selenization-sulfurization sequential steps: development of composition graded absorbers for low cost photovoltaic devices10.1016/j.matchemphys.2015.04.030 ↗
17. A comparative study of solution-processed low-and high-band-gap chalcopyrite thin-film solar cells10.1088/0022-3727/47/13/135105 ↗
18. Cu(In, Ga)(S, Se)2 thin film solar cell with 10.7% conversion efficiency obtained by selenization of the Na-doped spray-pyrolyzed sulfide precursor film10.1021/am507684x ↗
19. 10.3%-efficient submicron-thick Cu(In, Ga)Se2 solar cells with absorber fabricated by sputtering In2Se3, CuGaSe2 and Cu2Se targets10.1016/j.apsusc.2018.02.172 ↗
20. Structural characterization of coevaporated Cu(In, Ga)Se2 absorbers deposited at low temperature10.1016/j.jallcom.2019.04.135 ↗
21. Effect of gallium grading in Cu(In, Ga)Se2 solar-cell absorbers produced by multi-stage coevaporation10.1016/j.solmat.2010.10.011 ↗
22. Recrystallization of Cu(In, Ga)Se2 thin films studied by x-ray diffraction10.1016/j.actamat.2013.04.006 ↗
23. Growth and characterization of high quality CIGS films using novel precursors stacked and surface sulfurization process10.1007/s10854-018-9235-5 ↗
24. Se interlayer in CIGS absorption layer for solar cell devices10.1016/j.jallcom.2015.01.126 ↗
25. Efficiency improvement of CIGS solar cells by a modified rear contact10.1016/j.solener.2017.08.054 ↗
26. Cu(In, Ga)Se2 film formation from selenization of mixed metal/metal-selenide precursors10.1016/j.solmat.2009.11.004 ↗
27. Control of two-step growth processes of chalcopyrite thin films by x-ray fluorescence spectroscopy10.1016/S0169-4332(00)00876-X ↗
28. Study of the effect of gallium grading in Cu(In, Ga)Se210.1016/S0040-6090(99)00845-7 ↗
29. Effects of Ga accumulation on the microstructure of Cu(In1-x, Gax)Se2 thin films during selenization10.1016/j.jallcom.2013.06.177 ↗
30. Effect of the burn-out step on the microstructure of the solution-processed Cu(In, Ga)Se2 solar cells10.1016/j.tsf.2015.03.063 ↗
31. Ink formulation and low-temperature incorporation of sodium to yield 12% efficient Cu(In, Ga)(S, Se)2 solar cells from sulfide nanocrystal inks10.1002/pip.2200 ↗
32. Characteristics of Cu(In, Ga)Se2 films prepared by atmospheric pressure selenization of Cu-In-Ga precursors using ditert-butylselenide as Se source10.1149/2.021204jes ↗
33. Two-stage growth of smooth Cu(In, Ga)Se2 films using end-point detection10.1016/j.tsf.2004.11.076 ↗
34. Back surface band gap gradings in Cu(In, Ga)Se2 solar cells10.1016/S0040-6090(00)01726-0 ↗
35. Influence of shunt conduction on determining the dominant recombination processes in CIGS thin-film solar cells10.1016/j.cap.2012.06.006 ↗