Pretreatment of Lithium Surface by Using Iodic Acid (HIO₃) To Improve Its Anode Performance in Lithium Batteries

Iodic acid (HIO 3 ) was exploited as the effective source to build an artificial solid-electrolyte interphase (SEI) on the surface of Li anode. On one hand, HIO 3 is a weak solid-state acid and can be easily handled to remove most ion-insulating residues like Li 2 CO 3 and/or LiOH from the pristine Li surface; on the other hand, both the products of LiI and LiIO 3 resulted from the chemical reactions between Li metal and HIO 3 are reported to be the ion-conductive components. As a result, the lower voltage polarization and impedance, longer cycling lifetime and higher Coulombic efficiency have been successfully achieved in the HIO 3 -treated Li–Li and Li–Cu cells. By further using the HIO 3 -treated Li anode into practical Li–S batteries, the impressive results also have been obtained, with average discharge capacities of 719 mAh g –1 for 200 cycles (0.2 C) and 506 mAh g –1 for 500 cycles (0.5 C), which were better than the Li–S batteries using the pristine Li anode (552 and 401 mAh g –1, respectively) under the same conditions.