Adsorption and Association of a Symmetric PEO-PPO-PEO Triblock Copolymer on Polypropylene, Polyethylene, and Cellulose Surfaces

The association of a symmetric polyoxyethylene-polyoxypropylene-polyoxyethylene (PEO(19)-PPO(29)-PEO(19)) triblock copolymer adsorbed from aqueous solutions onto polypropylene (PP), polyethylene (PE), and cellulose surfaces was probed using Atomic Force Microscopy (AFM). Significant morphological differences between the polyolefin substrates (PP and PE) and the cellulose surfaces were observed after immersion of the films in the PEO(19)-PPO(29)-PEO(19) solutions. When the samples were scanned, while immersed in solutions of the triblock copolymer, it was revealed that the structures adsorbed on the polyolefin surfaces were smoothed by the adsorbed PEO(19)-PPO(29)-PEO(19). In contrast, those structures on the hydrophilic cellulose surfaces were sharpened. These observations were related to the roughness of the substrate and the energy of interaction between the surfaces and the PEO and PPO polymer segments. The interaction energy between each of the blocks and the surface was calculated using molecular dynamics simulations. It is speculated that the associative structures amply reported in aqueous solution at concentrations above the critical micelle concentration, CMC, are not necessarily preserved upon adsorption; instead, it appears that molecular arrangements of the anchor-buoy type and hemimicelles prevail. The reported data suggests that the roughness of the surface, as well as its degree of hydrophobicity, have a large influence on the nature of the resulting adsorbed layer. The reported observations are valuable in explaining the behavior of finishing additives and lubricants commonly used in textile and fiber processing, as well as the effect of the morphology of the boundary layers on friction and wear, especially in the case of symmetric triblock copolymers, which are commonly used as antifriction, antiwear additives.