Synthesis of Mesoporous Co²⁺-Doped TiO₂ Nanodisks Derived from Metal Organic Frameworks with Improved Sodium Storage Performance

TiO 2 is a most promising anode candidate for rechargeable Na-ion batteries (NIBs) because of its appropriate working voltage, low cost, and superior structural stability during chage/discharge process. Nevertheless, it suffers from intrinsically low electrical conductivity. Herein, we report an in situ synthesis of Co 2+ -doped TiO 2 through the thermal treatment of metal organic frameworks precursors of MIL-125(Ti)-Co as a superior anode material for NIBs. The Co 2+ -doped TiO 2 possesses uniform nanodisk morphology, a large surface area and mesoporous structure with narrow pore distribution. The reversible capacity, Coulombic efficiency (CE) and rate capability can be improved by Co 2+ doping in mesoporous TiO 2 anode. Co 2+ -doped mesoporous TiO 2 nanodisks exhibited a high reversible capacity of 232 mAhg –1 at 0.1 Ag 1–, good rate capability and cycling stability with a stable capacity of about 140 mAhg –1 at 0.5 Ag 1– after 500 cycles. The enhanced Na-ion storage performance could be due to the increased electrical conductivity revealed by Kelvin probe force microscopy measurements.