Multi-Scale Mechanical Behavior of the Li3PS4 Solid-Phase Electrolyte

Lauryn L. Baranowski, Chelsea M. Heveran, Virginia L. Ferguson, Conrad R. Stoldt

Publisher page

Abstract

The need for smaller, lighter, and longer lasting rechargeable batteries is projected to increase rapidly in the coming years because of high demand for portable electronics and electric vehicles. While traditional Li-ion batteries use liquid-phase electrolytes, these suffer from safety risks and low energy density. Solid-phase electrolytes can avoid these issues by enabling a Li metal anode, but tend to fail during cycling due to Li metal dendrite growth between the electrodes. Because Li dendrite nucleation and growth can be viewed in terms of the mechanical behavior of the battery components, it is critical to understand the mechanical response of candidate electrolyte materials. In this work, we use nanoindentation and bulk acoustic techniques to characterize the mechanical properties of β-Li 3 PS 4, a promising Li-ion conducting ceramic. We find that the bulk and shear moduli of an 80% dense bulk LPS sample are 10–12 GPa and 5–6 GPa, respectively. Although this value of shear modulus may be too low to prevent Li dendrite propagation, it is likely that there are many other mechanical properties that must be taken into account to fully understand Li dendrite nucleation and growth. Ultimately, this work represents a first step in understanding the relationship between Li 3 PS 4 separator manufacture and its mechanical properties.
Source: openalex_inverted_index · Quality: baseline

Research context

OpenAlex topics: Advanced Graph Theory Research · Complexity and Algorithms in Graphs · Interconnection Networks and Systems

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

Department of Mechanical Engineering, University of Colorado at Boulder, Boulder, Colorado 80309, United States

Funding

National Aeronautics and Space Administration

References (28)

Show source-provided references
1. 10.1039/C3EE40795K10.1039/C3EE40795K ↗
2. 10.1016/j.jpowsour.2010.01.07610.1016/j.jpowsour.2010.01.076 ↗
3. 10.1021/ja311089510.1021/ja3110895 ↗
4. 10.1038/nmat436910.1038/nmat4369 ↗
5. 10.1107/S002188981103897010.1107/S0021889811038970 ↗
6. 10.1149/1.185085410.1149/1.1850854 ↗
7. 10.2109/jcersj2.121.94610.2109/jcersj2.121.946 ↗
8. 10.1149/2.0061602jes10.1149/2.0061602jes ↗
9. 10.1021/acs.chemmater.5b0385410.1021/acs.chemmater.5b03854 ↗
10. 10.1016/j.jmps.2010.09.01210.1016/j.jmps.2010.09.012 ↗
11. 10.1111/j.1551-2916.2007.02012.x10.1111/j.1551-2916.2007.02012.x ↗
12. 10.1016/j.jbiomech.2010.10.00810.1016/j.jbiomech.2010.10.008 ↗
13. 10.1007/s10853-014-8682-510.1007/s10853-014-8682-5 ↗
14. 10.1016/j.actamat.2008.01.02110.1016/j.actamat.2008.01.021 ↗
15. 10.1016/j.msea.2013.11.04410.1016/j.msea.2013.11.044 ↗
16. 10.1016/j.eml.2016.03.00210.1016/j.eml.2016.03.002 ↗
17. 10.1016/j.ssi.2010.10.00110.1016/j.ssi.2010.10.001 ↗
18. 10.1557/jmr.2004.19.1.310.1557/jmr.2004.19.1.3 ↗
19. ASTM International · 2015
20. Courtney T. H. · 2005
21. 10.1038/nmat191110.1038/nmat1911 ↗
22. 10.1016/j.ceramint.2013.05.12210.1016/j.ceramint.2013.05.122 ↗
23. 10.1007/BF0173926910.1007/BF01739269 ↗
24. 10.1016/j.elecom.2015.05.00110.1016/j.elecom.2015.05.001 ↗
25. 10.1016/j.matlet.2013.01.02110.1016/j.matlet.2013.01.021 ↗
26. 10.1149/1.337463410.1149/1.3374634 ↗
27. 10.1149/2.049210jes10.1149/2.049210jes ↗
28. 10.1021/acs.jpclett.5b0163910.1021/acs.jpclett.5b01639 ↗