Improved Mechanical Stability of Dried Collagen Membrane after Metal Infiltration

Seung-Mo Lee, Eckhard Pippel, Oussama Moutanabbir, Ilja Gunkel, Thomas Thurn-Albrecht, Mato Knez

Publisher page

Abstract

A few percent of transition metals impregnated inside some biological organisms in nature remarkably improve such organisms' mechanical stability. Although the lure to emulate them for development of new biomimetic structural materials has been great, the practical advances have been rare because of the lack of proper synthetic approaches. Multiple pulsed vapor phase infiltration proved successful for the preparation of such transition metal impregnated materials with highly improved mechanical stability. The artificially infiltrated metals (Al, Ti, or Zn) from gas phase lead to around 3 times increase of toughness (in terms of breaking energy) of natural collagen in a dried state. In addition, the infiltrated metals apparently induce considerable crystallographic changes in the natural collagen structures. This infiltration approach can be used as guide for the synthesis of bioinspired structural materials related to metal infiltration.
Source: openalex_inverted_index · Quality: baseline

Research context

OpenAlex topics: Bone Tissue Engineering Materials · Collagen: Extraction and Characterization · Polymer Surface Interaction Studies

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

Max-Planck-Institut für Mikrostrukturphysik, Weinberg 2, D-06120 Halle, Germany, and Institut für Physik, Martin-Luther-Universität Halle-Wittenberg, D-06099 Halle, Germany

References (40)

Show source-provided references
1. Cribb B. W. · Naturwissenschaften · 2007 · 95 · 1710.1007/s00114-007-0288-1 ↗
2. Broomell C. C. · Acta Biomater. · 2008 · 4 · 204510.1016/j.actbio.2008.06.017 ↗
3. Broomell C. C. · J. Exp. Biol. · 2006 · 209 · 321910.1242/jeb.02373 ↗
4. Lee S.-M. · Science · 2009 · 324 · 48810.1126/science.1168162 ↗
5. Zhang L. · Angew. Chem., Int. Ed. · 2009 · 48 · 498210.1002/anie.200900426 ↗
6. Ricard-Blum S. · Top. Curr. Chem. · 2005 · 247 · 3510.1007/b103819 ↗
7. Ramachandran G. N. · Nature · 1955 · 176 · 59310.1038/176593a0 ↗
8. Rich A. · J. Mol. Biol. · 1961 · 3 · 48310.1016/S0022-2836(61)80016-8 ↗
9. Bella J. · Science · 1994 · 266 · 7510.1126/science.7695699 ↗
10. Fraser R. D. B. · J. Mol. Biol. · 1979 · 129 · 46310.1016/0022-2836(79)90507-2 ↗
11. Orgel J. P. R. O. · Proc. Natl. Acad. Sci. U. S. A. · 2006 · 103 · 900110.1073/pnas.0502718103 ↗
12. Gelse K. · Adv. Drug Delivery Rev. · 2003 · 55 · 153110.1016/j.addr.2003.08.002 ↗
13. Wong M. · Dev. Biol. · 1984 · 104 · 2810.1016/0012-1606(84)90033-2 ↗
14. Arias J. L. · Connect. Tissue Res. · 1991 · 26 · 3710.3109/03008209109152162 ↗
15. Nakano T. · Poult. Sci. · 2003 · 82 · 51010.1093/ps/82.3.510 ↗
16. There are many measurement techniques for the characterization of the mechanical properties of materials such as nanoindentation and AFM. Here, because the sample are not homogenous (collagen inner structure + outer metal oxide films), such techniques were not suitable. Therefore, even though it is a primitive method, the property characterization was performed by means of uniaxial tensile tests.
17. Rief M. · Science · 1997 · 276 · 110910.1126/science.276.5315.1109 ↗
18. Rief M. · J. Mol. Biol. · 1999 · 286 · 55310.1006/jmbi.1998.2466 ↗
19. Smith B. L. · Nature · 1999 · 399 · 76110.1038/21607 ↗
20. Oberhauser A. F. · Nature · 1998 · 393 · 18110.1038/30270 ↗
21. For the preparation of cross-sectioned sample, we were not able to find out any better method than FIB. Of course, during sectioning, metal (Al, Ti, or Zn) at a certain location might be sputtered out by the ion-beam and re-deposited at the adjacent location. Consequently, this might contribute to the background signal of Ti across the collagen fibril. However, Raman and X-ray analysis clearly confirmed the presence of the metal elements inside the collagen fibrils.
22. Fernández A. · Phys. Rev. Lett. · 2003 · 91 · 01810210.1103/PhysRevLett.91.018102 ↗
23. Cordier F. · J. Mol. Biol. · 2002 · 715 · 73910.1006/jmbi.2002.5446 ↗
24. Spadaro J. A. · Nature · 1970 · 225 · 113410.1038/2251134a0 ↗
25. Martin J. Y. · J. Biomed. Mater. Res. · 1995 · 29 · 38910.1002/jbm.820290314 ↗
26. Morra M. · Biomaterials · 2003 · 24 · 463910.1016/S0142-9612(03)00360-0 ↗
27. Müller R. · Biomaterials · 2006 · 27 · 405910.1016/j.biomaterials.2006.03.019 ↗
28. Rammelt S. · Biomaterials · 2006 · 27 · 556110.1016/j.biomaterials.2006.06.034 ↗
29. Yi F. · Biomaterials · 2004 · 25 · 459110.1016/j.biomaterials.2003.11.052 ↗
30. Frushour B. G. · Biopolymers · 1975 · 14 · 37910.1002/bip.1975.360140211 ↗
31. Cheng W.-T. · Microsc. Res. Tech. · 2005 · 68 · 7510.1002/jemt.20229 ↗
32. Further literature, which was used for peak assignments, can be found in Table S3 in theSupporting Information.
33. Beck K. · J. Struct. Biol. · 1998 · 122 · 1710.1006/jsbi.1998.3965 ↗
34. In the related literature, various reported shifts of the vibrational modes of titanium nitride, in particular in refs 37−42 in theSupporting Information, do not perfectly correspond or even show large differences. In addition, Raman shifts at 578, 488, and 338 cm−1show poor relevance to the shifts of amorphous TiO2in the literature.
35. The location of peaks A, B, and C are close to diffraction peaks of calcite. For the experiments we used collagen membranes extracted from the air-cell region of the hen’s egg (see Experimental Section). Decisively, as shown by EDX data in Figure3B, Ca elements were not detected. Therefore, these peaks presumably do not originate from calcite.
36. Charulatha V. · Biomaterials · 2003 · 24 · 75910.1016/S0142-9612(02)00412-X ↗
37. Rajini K. H. · J. Mater. Sci. · 2001 · 36 · 558910.1023/A:1012509514714 ↗
38. Buehler M. J. · J. Mater. Res. · 2006 · 21 · 194710.1557/jmr.2006.0236 ↗
39. Buehler M. J. · Proc. Natl. Acad. Sci. U.S.A. · 2006 · 103 · 1228510.1073/pnas.0603216103 ↗
40. Place E. S. · Nat. Mater. · 2009 · 8 · 45710.1038/nmat2441 ↗