Facile synthesis of highly branched jacks-like ZnO nanorods and their applications in dye-sensitized solar cells

Graphical abstract: -- Abstract: Highly branched, jacks-like ZnO nanorods architecture were explored as a photoanode in dye-sensitized solar cells, and their photovoltaic performance was compared with that of branch-free ZnO nanorods photoanodes. The highly branched network and large pores of the jacks-like ZnO nanorods electrodes enhances the charge transport, and electrolyte penetration. Thus, the jacks-like ZnO nanorods DSSCs render a higher conversion efficiency of {eta} = 1.82% (V{sub oc} = 0.59 V, J{sub sc} = 5.52 mA cm{sup -2}) than that of the branch-free ZnO nanorods electrodes ({eta} = 1.08%, V{sub oc} = 0.49 V, J{sub sc} = 4.02 mA cm{sup -2}). The incident photon-to-current conversion efficiency measurements reveal that the jacks-like ZnO nanorods DSSCs exhibit higher internal quantum efficiency ({approx}59.1%) than do the branch-free ZnO nanorods DSSC ({approx}52.5%). The charge transfer resistances at the ZnO/dye/electrolyte interfaces investigated using electrochemical impedance spectroscopy showed that the jacks-like ZnO nanorods DSSC had high charge transfer resistance and a slightly longer electron lifetime, thus improving the solar-cell performance.