Boosting Hole Mobility: Indenofluorene-Arylamine Copolymers and Their Impact on Solution-Processed OLED Performance

We introduce three newly designed thermally cross-linkable hole transport copolymers ( PIF-TPD, PIF-F2PCz, and PIF-TPAPCz ) for improving the performance of solution-processed organic light-emitting diodes ( s -OLEDs). These copolymers, designed through a strategic molecular approach with benzocyclobutene (BCB) and styrene-based cross-linking monomers, show high solvent resistance at a low cross-linking temperature (150 °C). Furthermore, these conjugated copolymers based on planar indenofluorene with three different hole transport (HT) units, exhibit outstanding charge carrier mobility (1.61 × 10 –2 cm 2 V –1 s –1 ), demonstrated by comparing hole reorganization energy and electronic coupling strength of HT units. Despite these copolymers showing the overall vertical orientation in the horizontal dipole moment measurement results, we demonstrated that the HT units can exhibit the preferred orientation, contributing to high hole transport properties. As a result, they perform exceptionally well as hole transport layers in green phosphorescent s -OLEDs, achieving a maximum external quantum efficiency of 15.3% and a maximum current efficiency of 53.9 cd A –1 with a small efficiency roll-off despite their relatively low triplet energy levels. These results are comparable to vacuum-deposited OLEDs, highlighting the potential of these copolymers in advancing OLED technology for display panels and lighting applications.