Ca-MOF-Derived Porous Sorbents for High-Yield Solar-Driven Atmosphere Water Harvesting

The development of high-yield, metal–organic framework (MOF)-based water harvesters in arid areas remains challenging due to the absence of effective strategies for enhancing water sorption capacity and kinetics. Herein, we presented a novel strategy for in situ fabrication of calcium chloride (CaCl 2 ) decorated MOF-derived porous sorbents (PCC-42) through pyrolysis Ca-MOF and subsequently hydrochloric acid (HCl) vapor treatment process. The resulting PCC-42 sorbents exhibited a high water adsorption capacity of 3.04 g g –1 at 100% relative humidity (RH), outstanding photothermal performance, and rapid water uptake-release kinetics, surpassing most reported MOFs adsorbents. At 20, 30, 40, and 50% RH, PCC-42 demonstrated water uptake capacity of 0.45, 0.59, 0.76, and 0.9 g g –1, which represented an increase of 421 and 940% (at 20% RH) and 333 and 351% (at 30% RH) compared to Ca-MOF and CaCl 2 ·2H 2 O, respectively. Approximately 80% of the adsorbed water in PCC-42 could be released under one sun within 50 min. Indoor water harvesting experiments demonstrated that PCC-42 is a promising adsorbent for various humidity environments. Additionally, outdoor solar-driven atmospheric water harvesting (AWH) tests revealed a high daily water production of 1.13 L/kg adsorbent under typical arid conditions (30–60% RH). The proposed strategy helps the design of high-performance adsorbents for solar-driven AWH in arid environments.