Highly Resilient Dual-Crosslinked Hydrogel Adhesives Based on a Dopamine-Modified Crosslinker

Hydrogels are promising material for wound dressing and tissue engineering. However, owing to their low tissue adhesion in a moist environment and lack of flexibility, hydrogels are still not widely applied in movable parts, such as joints. Herein, we report a dual-crosslinked hydrogel adhesive using a dopamine-modified and acrylate-terminated crosslinker, tri(ethylene glycol) diacrylate-dopamine crosslinker (TDC). The covalent crosslinking was formed by photopolymerization between acrylic acid (AA) and TDC, and the noncovalent crosslinking was formed by intermolecular dopamine-dopamine and dopamine-AA interactions. Our resultant hydrogel demonstrated strong tissue adhesion in a moist environment (approximately 71 kPa) and high mechanical resilience (approximately 94%) with immediate recovery at a 200% strain rate. Moreover, it accelerated wound healing upon dressing the wound site properly. Our study provides the potential for advanced polymer synthesis by introducing a functional crosslinking agent.