Ce-Doped La₃Si_6.5Al_1.5N_9.5O_5.5, a Rare Highly Efficient Blue-Emitting Phosphor at Short Wavelength toward High Color Rendering White LED Application

Phase pure nondoped and Ce doped La 3 Si 6.5 Al 1.5 N 9.5 O 5.5 (Al containing La N-phase) samples have been obtained by solid-state reaction synthesis for the first time. 1% Ce-doped La 3 Si 6.5 Al 1.5 N 9.5 O 5.5 phosphor displays a broad excitation band ranging from UV to 410 nm, with a maximum at 355 nm. UV light excitation results in a narrow Ce 3+ 5d-4f emission band (fwhm = 68 nm) centered at 418 nm. The emission can be tuned from 417 nm at 0.5% Ce to 450 nm at 50% Ce. A high internal quantum efficiency up to 84% is achieved for a 1% Ce doped sample, which has CIE chromaticity coordinates of x = 0.157 and y = 0.069, close to the NTSC blue standard ( x = 0.155; y = 0.070). Compared to La 3 Si 8 O 4 N 11:Ce phosphor, the quantum efficiency and thermal stability have been enhanced for La 3 Si 6.5 Al 1.5 N 9.5 O 5.5:Ce phosphor without shifting the emission peak wavelength. La 3 Si 6.5 Al 1.5 N 9.5 O 5.5:Ce shows less thermal quenching than La 3 Si 8 O 4 N 11:Ce and no shift or change in the shape of emission spectra with increasing the temperature from 4 to 573 K. These results show that La 3 Si 6.5 Al 1.5 N 9.5 O 5.5:Ce is more efficient than any other (oxy-)nitride phosphor with an emission in the short wavelength blue region (400–450 nm). A white LED was fabricated using the La 3 Si 6.5 Al 1.5 N 9.5 O 5.5:5%Ce as a blue phosphor. The high color rendering index (Ra = 93.2, R9 = 91.4, and R12 = 89.5) obtained shows that the phosphor is a very promising conversion phosphor for white LEDs.