Study of Lithium Silicide Nanoparticles as Anode Materials for Advanced Lithium Ion Batteries

High Resolution Image Download MS PowerPoint Slide The development of high-performance silicon anodes for the next generation of lithium ion batteries (LIBs) evokes increasing interest in studying its lithiated counterpart—lithium silicide (Li x Si). In this paper we report a systematic study of three thermodynamically stable phases of Li x Si ( x = 4.4, 3.75, and 2.33) plus nitride-protected Li 4.4 Si, which are synthesized via the high-energy ball-milling technique. All three Li x Si phases show improved performance over that of unmodified Si, where Li 4.4 Si demonstrates optimum performance with a discharging capacity of 3306 (mA h)/g initially and maintains above 2100 (mA h)/g for over 30 cycles and above 1200 (mA h)/g for over 60 cycles at the current density of 358 mA/g of Si. A fundamental question studied is whether different electrochemical paradigms, that is, delithiation first or lithiation first, influence the electrode performance. No significant difference in electrode performance is observed. When a nitride layer (Li x N y Si z ) is created on the surface of Li 4.4 Si, the cyclability is improved to retain the capacity above 1200 (mA h)/g for more than 80 cycles. By increasing the nitridation extent, the capacity retention is improved significantly from the average decrease of 1.06% per cycle to 0.15% per cycle, while the initial discharge capacity decreases due to the inactivity of Si in the Li x N y Si z layer. Moreover, the Coulombic efficiencies of all Li x Si-based electrodes in the first cycle are significantly higher than that of a Si electrode (∼90% vs 40–70%).