Ultrafast and Stable CO₂ Capture Using Alkali Metal Salt-Promoted MgO–CaCO₃ Sorbents

As a potential candidate for precombustion CO2 capture at intermediate temperatures (200–400 °C), MgO-based sorbents usually suffer from low kinetics and poor cyclic stability. Herein, a general and facile approach is proposed for the fabrication of high-performance MgO-based sorbents via incorporation of CaCO3 into MgO followed by deposition of a mixed alkali metal salt (AMS). The AMS-promoted MgO–CaCO3 sorbents are capable of adsorbing CO2 at an ultrafast rate, high capacity, and good stability. The CO2 uptake of sorbent can reach as high as above 0.5 gCO2 gsorbent–1 after only 5 min of sorption at 350 °C, accounting for vast majority of the total uptake. In addition, the sorbents are very stable even under severe but more realistic conditions (desorption in CO2 at 500 °C), where the CO2 uptake of the best sorbent is stabilized at 0.58 gCO2 gsorbent–1 in 20 consecutive cycles. The excellent CO2 capture performance of the sorbent is mainly due to the promoting effect of molten AMS, the rapid formation of CaMg(CO3)2, and the plate-like structure of sorbent. The exceptional ultrafast rate and the good stability of the AMS-promoted MgO–CaCO3 sorbents promise high potential for practical applications, such as precombustion CO2 capture from integrated gasification combined cycle plants and sorption-enhanced water gas shift process.