Hydrothermal Synthesis and Catalytic Application of Ultrathin Rhodium Nanosheet Nanoassemblies

Ultrathin noble metal nanosheets with atomic thickness exhibit abnormal electronic, surfacial, and photonic properties due to the unique two-dimensional (2D) confinement effect, which have attracted intensive research attention in catalysis/electrocatalysis. In this work, the well-defined ultrathin Rh nanosheet nanoassemblies with dendritic morphology are synthesized by a facile hydrothermal method with assistance of poly(allylamine hydrochloride) (PAH), where PAH effectively acts as the complexant and shape-directing agent. Transmission electron microscopy and atomic force microscopy images reveal the thickness of 2D Rh nanosheet with (111) planes is only ca. 0.8–1.1 nm. Nitrogen adsorption–desorption measurement displays the specific surface area of the as-prepared ultrathin Rh nanosheet nanoassemblies is 139.4 m 2 g –1, which is much bigger than that of homemade Rh black (19.8 m 2 g –1 ). Detailed catalytic investigations display the as-prepared ultrathin Rh nanosheet nanoassemblies have nearly 20.4-fold enhancement in mass-activity for the hydrolysis of ammonia borane as compared with homemade Rh black.