Constructing a Multiple Covalent Interface and Isolating a Dispersed Structure in Silica/Rubber Nanocomposites with Excellent Dynamic Performance

Junchi Zheng, Dongli Han, Suhe Zhao, Xin Ye, Yiqing Wang, Youping Wu, Dong Dong, Jun Liu, Xiaohui Wu, Liqun Zhang

ACS Applied Materials & Interfaces· Volume 10· Issue 23
Publisher page

Abstract

Realizing and manipulating a fine dispersion of silica nanoparticles (NPs) in the polymer matrix is always a great challenge. In this work, we first successfully synthesized N, N'-bis[3-(triethoxysilyl)propyl-isopropanol]-propane-1,3-diamine (TSPD), which was a new interface modifier, aiming to promote the dispersion of silica NPs. Through Fourier transform infrared spectroscopy, nuclear magnetic resonance analysis, and mass spectroscopy, we verified that TSPD contains together six ethoxy groups at its two ends. Then, we used this TSPD to modify the pure silica NPs, and this modified silica was abbreviated as D-MS, which is realized by the thermal gravimetric analysis examination, scanning electron microscopy analysis, and dynamic light scattering results. It was clearly observed that D-MS NPs are connected to one another but are not conglutinated tightly, exhibiting a novel predispersed structure with around 1-2 nm certain extent of interparticle distance. Next, we fabricated the following four elastomer nanocomposites such as pure silica/natural rubber (NR) composite (PS-NR), D-MS/NR composite (DMS-NR), bis-(γ-triethoxysilylpropyl)-tetrasulfide (TESPT)-modified silica/NR composite (TS-NR), and TESPT-modified D-MS/NR composite (T&DMS-NR) and found that the Payne effect is the smallest for T&DMS-NR via the combination use of the D-MS and the traditional coupling agent TESPT, which is attributed to its best dispersion state evidenced by the transmission electron microscopy results. Moreover, by measuring a series of other important mechanical performances such as the stress-strain curve, the dynamic strain dependence of the loss factor, and the heat build-up, we concluded that the T&DMS-NR system greatly exceeds those of the three other rubber composites. In general, this new approach provides a good opportunity to prepare a silica/rubber composite with excellent properties in mechanical strength and dynamic behavior by tailoring the fine dispersion of NPs.
Source: openalex_inverted_index · Quality: baseline

Research context

OpenAlex topics: Polymer composites and self-healing · Polymer Nanocomposites and Properties · Dielectric materials and actuators

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

Beijing Red Avenue Innova Co., Ltd., Unit 1, 2, 3, Building 10, No. 20 Kechuang Fourteenth Street, Beijing Economic-Technological Development Area (BDA), Beijing 100176, PR China

References (49)

Show source-provided references
1. 10.1016/j.jiec.2012.04.01510.1016/j.jiec.2012.04.015 ↗
2. 10.1016/j.nanoen.2016.08.00210.1016/j.nanoen.2016.08.002 ↗
3. 10.1002/app.4533410.1002/app.45334 ↗
4. 10.1016/s0261-3069(00)00103-510.1016/s0261-3069(00)00103-5 ↗
5. 10.1021/acs.iecr.6b0351710.1021/acs.iecr.6b03517 ↗
6. 10.1021/acs.iecr.5b0314610.1021/acs.iecr.5b03146 ↗
7. 10.5254/1.354768110.5254/1.3547681 ↗
8. 10.1016/j.polymertesting.2014.06.00410.1016/j.polymertesting.2014.06.004 ↗
9. 10.1002/app.3422110.1002/app.34221 ↗
10. 10.1016/j.polymer.2014.02.06710.1016/j.polymer.2014.02.067 ↗
11. 10.1016/j.msea.2005.03.01210.1016/j.msea.2005.03.012 ↗
12. 10.1002/polb.2062210.1002/polb.20622 ↗
13. 10.1021/am501485810.1021/am5014858 ↗
14. 10.1021/am900540x10.1021/am900540x ↗
15. 10.1021/am503060n10.1021/am503060n ↗
16. 10.1021/am100279v10.1021/am100279v ↗
17. 10.1021/la305156s10.1021/la305156s ↗
18. 10.1021/jp709759e10.1021/jp709759e ↗
19. 10.1021/acsami.6b1513910.1021/acsami.6b15139 ↗
20. 10.1021/am506260j10.1021/am506260j ↗
21. 10.1021/ie020914p10.1021/ie020914p ↗
22. 10.1021/am504426j10.1021/am504426j ↗
23. 10.1016/s0169-4332(00)00828-x10.1016/s0169-4332(00)00828-x ↗
24. 10.1016/j.colsurfa.2012.11.05710.1016/j.colsurfa.2012.11.057 ↗
25. 10.1016/j.compositesa.2010.03.00510.1016/j.compositesa.2010.03.005 ↗
26. 10.1016/j.polymertesting.2004.05.00810.1016/j.polymertesting.2004.05.008 ↗
27. 10.1016/j.colsurfa.2010.01.05110.1016/j.colsurfa.2010.01.051 ↗
28. 10.1016/j.colsurfa.2015.07.04210.1016/j.colsurfa.2015.07.042 ↗
29. 10.1002/adma.20070009810.1002/adma.200700098 ↗
30. 10.1016/S0927-7757(02)00137-110.1016/S0927-7757(02)00137-1 ↗
31. 10.1007/s10853-008-3170-410.1007/s10853-008-3170-4 ↗
32. 10.1002/adfm.20130226110.1002/adfm.201302261 ↗
33. 10.1016/j.jcis.2004.08.06110.1016/j.jcis.2004.08.061 ↗
34. 10.1016/j.colsurfa.2008.07.05310.1016/j.colsurfa.2008.07.053 ↗
35. 10.1021/acs.iecr.7b0225010.1021/acs.iecr.7b02250 ↗
36. 10.1021/la026803c10.1021/la026803c ↗
37. 10.1002/adma.20120018410.1002/adma.201200184 ↗
38. Kim K.-J. · J. Ind. Eng. Chem. · 1991 · 7 · 50
39. 10.1016/j.polymertesting.2014.01.00210.1016/j.polymertesting.2014.01.002 ↗
40. 10.1016/j.powtec.2011.11.02310.1016/j.powtec.2011.11.023 ↗
41. 10.1016/j.polymertesting.2013.11.00910.1016/j.polymertesting.2013.11.009 ↗
42. 10.1016/j.msea.2005.03.01210.1016/j.msea.2005.03.012 ↗
43. 10.1016/j.compositesb.2015.07.00110.1016/j.compositesb.2015.07.001 ↗
44. 10.1021/ie301268e10.1021/ie301268e ↗
45. 10.1039/c7cp01453h10.1039/c7cp01453h ↗
46. 10.1016/j.jiec.2010.03.03010.1016/j.jiec.2010.03.030 ↗
47. 10.1002/app.1962.07006190610.1002/app.1962.070061906 ↗
48. 10.1016/j.eurpolymj.2014.02.01510.1016/j.eurpolymj.2014.02.015 ↗
49. 10.1002/app.2185510.1002/app.21855 ↗