Mechanical Enhancement of Bioinspired Polydopamine Nanocoatings

Inspired by the catechol and amine-rich adhesive proteins of mussels, polydopamine (pDA) has become one of the most widely employed methods for functionalizing material surfaces, powered in part by the versatility and simplicity of pDA film deposition that takes place spontaneously on objects immersed in an alkaline aqueous solution of dopamine monomer. Despite the widespread adoption of pDA as a multifunctional coating for surface modification, it exhibits poor mechanical performance. Attempts to modify the physical properties of pDA by incorporation of oxidizing agents, cross-linkers, or carbonization of the films at ultrahigh temperatures have been reported; however, improving mechanical properties with mild post-treatments without sacrificing the functionality and versatility of pDA remains a challenge. Here, we demonstrate thermal annealing at a moderate temperature (130 °C) as a facile route to enhance mechanical robustness of pDA coatings. Chemical spectroscopy, X-ray scattering, molecular force spectroscopy, and bulk mechanical analyses indicate that monomeric and oligomeric species undergo further polymerization during thermal annealing, leading to fundamental changes in molecular and bulk mechanical behavior of pDA. Considerable improvements in scratch resistance were noted in terms of both penetration depth (32% decrease) and residual depth (74% decrease) for the annealed pDA coating, indicating the enhanced ability of the annealed coating to resist mechanical deformations. Thermal annealing resulted in significant enhancement in the intermolecular and cohesive interactions between the chains in the pDA structure, attributed to cross-linking and increased entanglements, preventing desorption and detachment of the chains from the coating. Importantly, improvements in pDA mechanical performance through thermal annealing did not compromise the ability of pDA to support secondary coating reactions as evidenced by electroless deposition of a metal film adlayer on annealed pDA.