Enhanced Electrochemical Performances of Bi₂O₃/rGO Nanocomposite via Chemical Bonding as Anode Materials for Lithium Ion Batteries

Bismuth oxide/reduced graphene oxide (termed Bi 2 O 3 @rGO) nanocomposite has been facilely prepared by a solvothermal method via introducing chemical bonding that has been demonstrated by Raman and X-ray photoelectron spectroscopy spectra. Tremendous single-crystal Bi 2 O 3 nanoparticles with an average size of ∼5 nm are anchored and uniformly dispersed on rGO sheets. Such a nanostructure results in enhanced electrochemical reversibility and cycling stability of Bi 2 O 3 @rGO composite materials as anodes for lithium ion batteries in comparison with agglomerated bare Bi 2 O 3 nanoparticles. The Bi 2 O 3 @rGO anode material can deliver a high initial capacity of ∼900 mAh/g at 0.1 C and shows excellent rate capability of ∼270 mAh/g at 10 C rates (1 C = 600 mA/g). After 100 electrochemical cycles at 1 C, the Bi 2 O 3 @rGO anode material retains a capacity of 347.3 mAh/g with corresponding capacity retention of 79%, which is significantly better than that of bare Bi 2 O 3 material. The lithium ion diffusion coefficient during lithiation–delithiation of Bi 2 O 3 @rGO nanocomposite has been evaluated to be around ∼10 –15 –10 –16 cm 2 /S. This work demonstrates the effects of chemical bonding between Bi 2 O 3 nanoparticles and rGO substrate on enhanced electrochemical performances of Bi 2 O 3 @rGO nanocomposite, which can be used as a promising anode alterative for superior lithium ion batteries.