Modulation of the Optical Properties of Monolayer WS2 by the Single-Atom Sites
Source abstract
Abstract
Monolayer tungsten disulfide (ML WS 2 ) exhibits remarkable optical and electrical properties, but its limited light absorption hinders its application in next-generation sensors and optical detectors. Therefore, it is vital to design mixed-dimensional heterostructure (MDH) interfaces that enhance overall absorption and facilitate the effective transfer of photogenerated carriers simultaneously. In this study, MDHs consisting of zero-dimensional (0D) single-site single-tungsten-atom oxides (STAOs) and two-dimensional (2D) ML WS 2 were successfully constructed. The optical properties of ML WS 2 have been comprehensively characterized by using a series of optical techniques including absorption, photoluminescence (PL), and Raman techniques. In comparison to the case of ML WS 2, both geometric configurations (WS 2 /STAO/SiO 2 and STAO/WS 2 /SiO 2 ) show similar results in the absorption and PL spectra: the absorption of the heterostructures is enhanced, and meanwhile, STAOs significantly reduce the PL intensity of the A-exciton in ML WS 2, while increasing the trion-to-exciton intensity ratio. These results suggest that a charge transfer process may occur between STAO and WS 2 due to the formation of heterostructures interactions. In order to confirm the existence of the charge transfer, copper phthalocyanine (CuPc) has been chosen as target molecules in surface-enhanced Raman spectroscopy (SERS) experiments for both geometric configurations. It is interesting to see that Raman signals of CuPc show almost no enhancement and sometimes even the quenching effect in the case of STAO/WS 2, while in the case of WS 2 /STAO, they exhibit an STAOs amount-dependent exponential enhancement trend, with an enhancement factor up to ∼37 at 1531 cm –1 peak. Furthermore, Vienna Ab initio Simulation Package (VASP) theoretical calculations confirm that electrons can efficiently transfer from STAO to WS 2, which is consistent with our experimental results. Our work demonstrates a method for tuning the optical properties of 2D materials via single sites, providing new strategies and evidence for employing MDHs in sensitive and multifunctional optoelectronic devices.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: 2D Materials and Applications · Perovskite Materials and Applications · Gold and Silver Nanoparticles Synthesis and Applications
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Key Laboratory of Luminescence and Optical Information, Ministry of Education, Institute of Optoelectronic Technology
Beijing Jiaotong University
Beijing Key Laboratory of Microstructure and Properties of Solids, Faculty of Materials and Manufacturing
Beijing University of Technology
Funding
National Key Research and Development Program of China · Natural Science Foundation of Beijing Municipality · National Natural Science Foundation of China
References (57)
Show source-provided references
1. 10.3390/molecules2914334110.3390/molecules29143341 ↗
2. 10.1039/C5NR01205H10.1039/C5NR01205H ↗
3. 10.1002/advs.20230516210.1002/advs.202305162 ↗
4. 10.1021/nl302635710.1021/nl3026357 ↗
5. 10.1021/nn305275h10.1021/nn305275h ↗
6. 10.1021/nn502362b10.1021/nn502362b ↗
7. 10.1002/adma.20150222210.1002/adma.201502222 ↗
8. 10.1007/s12274-014-0602-010.1007/s12274-014-0602-0 ↗
9. 10.1038/srep1069910.1038/srep10699 ↗
10. 10.1088/2632-959X/ac022b10.1088/2632-959X/ac022b ↗
11. 10.1016/j.progsurf.2021.10062610.1016/j.progsurf.2021.100626 ↗
12. Zhang Z. · 202210.1002/9783527833887 ↗
13. Huang Y. · Nat. Commun. · 2020 · 11 · 245310.1038/s41467-020-16266-w ↗
14. 10.1021/acsnano.0c0675010.1021/acsnano.0c06750 ↗
15. 10.1007/s12274-017-1941-410.1007/s12274-017-1941-4 ↗
16. 10.1021/acs.nanolett.0c0049210.1021/acs.nanolett.0c00492 ↗
17. 10.1016/j.mtnano.2021.10011210.1016/j.mtnano.2021.100112 ↗
18. 10.1038/nmat470310.1038/nmat4703 ↗
19. 10.1016/j.mssp.2023.10759810.1016/j.mssp.2023.107598 ↗
20. 10.1002/smtd.20230024510.1002/smtd.202300245 ↗
21. 10.1016/j.apmt.2022.10171710.1016/j.apmt.2022.101717 ↗
22. 10.1016/j.mee.2022.11192610.1016/j.mee.2022.111926 ↗
23. 10.1002/adfm.20180201510.1002/adfm.201802015 ↗
24. 10.1002/adfm.20240995110.1002/adfm.202409951 ↗
25. 10.1021/acsami.9b0397110.1021/acsami.9b03971 ↗
26. 10.1016/j.cej.2024.15586110.1016/j.cej.2024.155861 ↗
27. 10.1038/s41467-023-38198-x10.1038/s41467-023-38198-x ↗
28. 10.1038/s41467-023-43928-210.1038/s41467-023-43928-2 ↗
29. 10.1002/adma.20210907410.1002/adma.202109074 ↗
30. 10.1007/s40843-022-1968-510.1007/s40843-022-1968-5 ↗
31. 10.1002/adma.20190349110.1002/adma.201903491 ↗
32. 10.1021/nn305275h10.1021/nn305275h ↗
33. 10.1021/acsnano.5b0172710.1021/acsnano.5b01727 ↗
34. 10.1021/nn502362b10.1021/nn502362b ↗
35. 10.1021/acsnano.0c0743010.1021/acsnano.0c07430 ↗
36. 10.3390/nano809072510.3390/nano8090725 ↗
37. 10.1557/jmr.2016.4710.1557/jmr.2016.47 ↗
38. 10.1021/nn504196n10.1021/nn504196n ↗
39. 10.1039/C4CS00282B10.1039/C4CS00282B ↗
40. 10.1039/c3nr03052k10.1039/c3nr03052k ↗
41. 10.1038/ncomms1327910.1038/ncomms13279 ↗
42. 10.1021/acs.nanolett.8b0179310.1021/acs.nanolett.8b01793 ↗
43. 10.1016/0022-4073(77)90161-310.1016/0022-4073(77)90161-3 ↗
44. 10.1016/j.optlastec.2006.03.01110.1016/j.optlastec.2006.03.011 ↗
45. 10.1021/jacs.5b1014410.1021/jacs.5b10144 ↗
46. 10.1016/j.saa.2006.10.01310.1016/j.saa.2006.10.013 ↗
47. 10.1021/j100276a01710.1021/j100276a017 ↗
48. 10.1002/adma.20231234810.1002/adma.202312348 ↗
49. 10.1016/S1872-5805(21)60098-510.1016/S1872-5805(21)60098-5 ↗
50. 10.1021/nn101091410.1021/nn1010914 ↗
51. 10.1002/adma.20241197210.1002/adma.202411972 ↗
52. 10.1021/acs.nanolett.7b0041210.1021/acs.nanolett.7b00412 ↗
53. 10.1021/jp308844710.1021/jp3088447 ↗
54. 10.1002/smll.20100091810.1002/smll.201000918 ↗
55. 10.1002/smll.20110222310.1002/smll.201102223 ↗
56. 10.1021/acs.jpcc.9b0406310.1021/acs.jpcc.9b04063 ↗
57. 10.1063/1.170485310.1063/1.1704853 ↗