High-Performance Monolithic Photovoltaic–Thermoelectric Hybrid Power Generator Using an Exothermic Reactive Interlayer
Source abstract
Abstract
A high-performance monolithic photovoltaic–thermoelectric hybrid generator with a photothermal conversion layer is introduced. The layer, a thin acrylic film dyed with black colored AZO dye, effectively absorbs photons in the near-infrared region. The AZO dye supports an exothermic reaction through nonradiative relaxation. The hybrid generator was fabricated through monolithic integration. A thermoelectric (TE) module was fabricated directly on the back surface of the photovoltaic (PV) module without using the ceramic substrate typically employed in conventional TE modules, so that thermal resistance between the PV module and TE module could be minimized. The 51.35 cm2 fabricated hybrid generator showed a power conversion efficiency of about 22.5% with an open-circuit voltage of 0.94 V and a maximum power of 1.15 W under standard AM 1.5G illumination. The hybrid power generator with the photothermal conversion layer showed about 40% higher output power compared to the control PV only, about 16% higher than an acrylic control film, and about 7.4% higher than a common black dyed interface layer.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Advanced Thermoelectric Materials and Devices · Thermal Radiation and Cooling Technologies · Perovskite Materials and Applications
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
School of Electrical Engineering, Korea Advanced Institute of Science and Technology (KAIST), 291 Daehak-ro, Yuseong-gu, Daejeon 34141, Republic of Korea
Solar Energy Laboratory, Korea Institute of Energy Research, 140 Yuseong-daero, 1312 Beon-gil, Yuseong-gu, Daejeon 31401, Republic of Korea
Funding
National Research Foundation of Korea
References (31)
Show source-provided references
1. 10.1002/aenm.20170338510.1002/aenm.201703385 ↗
2. 10.1002/aenm.20170222110.1002/aenm.201702221 ↗
3. 10.1016/j.solmat.2018.06.02010.1016/j.solmat.2018.06.020 ↗
4. 10.1038/nenergy.2017.3210.1038/nenergy.2017.32 ↗
5. 10.1016/j.solener.2016.12.00710.1016/j.solener.2016.12.007 ↗
6. 10.1039/C7EE00286F10.1039/C7EE00286F ↗
7. 10.1016/j.solmat.2017.03.01710.1016/j.solmat.2017.03.017 ↗
8. 10.1016/j.renene.2017.11.09210.1016/j.renene.2017.11.092 ↗
9. 10.1016/j.enconman.2016.03.02310.1016/j.enconman.2016.03.023 ↗
10. 10.1016/j.energy.2016.01.05510.1016/j.energy.2016.01.055 ↗
11. 10.1016/j.enconman.2017.09.03610.1016/j.enconman.2017.09.036 ↗
12. 10.1016/j.enconman.2018.06.01210.1016/j.enconman.2018.06.012 ↗
13. 10.1016/j.energy.2015.12.02410.1016/j.energy.2015.12.024 ↗
14. 10.1016/j.enconman.2015.07.00710.1016/j.enconman.2015.07.007 ↗
15. 10.1002/pip.247510.1002/pip.2475 ↗
16. 10.1016/j.enconman.2015.12.06910.1016/j.enconman.2015.12.069 ↗
17. 10.1063/1.493142810.1063/1.4931428 ↗
18. 10.1016/j.energy.2017.03.04210.1016/j.energy.2017.03.042 ↗
19. 10.1002/aenm.20170293710.1002/aenm.201702937 ↗
20. 10.1038/srep0212310.1038/srep02123 ↗
21. 10.1016/j.solener.2012.12.00210.1016/j.solener.2012.12.002 ↗
22. 10.1016/j.enconman.2016.02.06110.1016/j.enconman.2016.02.061 ↗
23. 10.1016/j.solener.2018.04.05210.1016/j.solener.2018.04.052 ↗
24. 10.1021/acs.chemmater.7b0285310.1021/acs.chemmater.7b02853 ↗
25. 10.1021/acsenergylett.7b0060810.1021/acsenergylett.7b00608 ↗
26. 10.1039/C5EE01363A10.1039/C5EE01363A ↗
27. 10.1002/aenm.20160014810.1002/aenm.201600148 ↗
28. 10.1016/j.jphotochem.2005.07.02510.1016/j.jphotochem.2005.07.025 ↗
29. 10.1039/b211260d10.1039/b211260d ↗
30. 10.1002/anie.20080525710.1002/anie.200805257 ↗
31. 10.1002/adma.20140083110.1002/adma.201400831 ↗