Solution-Processed, Silver-Doped NiOx as Hole Transporting Layer for High-Efficiency Inverted Perovskite Solar Cells

Jianghui Zheng, Long Hu, Jae S. Yun, Meng Zhang, Cho Fai Jonathan Lau, Jueming Bing, Xiaofan Deng, Qingshan Ma, Yongyoon Cho, Weifei Fu, Chao Chen, Martin A. Green, Shujuan Huang, Anita W. Y. Ho-Baillie

ACS Applied Energy Materials· Volume 1· Issue 2

Abstract

NiO x is as a promising hole transporting layer (HTL) for perovskite solar cells (PSCs) due to its good stability, large bandgap, and deep valence band. The use of NiO x as a HTL for “inverted” PSC as part of a monolithic silicon/perovskite tandem solar cell is also suitable when the processing temperature is suitably low. Solution-processed NiO x at low temperature for PSCs remains to be improved due to the relatively low short-circuit current density ( J sc ) and fill factor (FF) of reported devices. In this work, the use of Ag-doping is reported for solution-processed NiO x film at 300 °C for inverted planar PSCs. We have shown that Ag-doping has no negative effect on the optical transmittance and morphology of the NiO x film and the overlying perovskite film. In addition, Ag-doping is effective in improving conductivity, improving carrier extraction, and enhancing the p-type property of the NiO x film confirmed by electrical characterization, photoluminescence measurements, and ultraviolet photoelectron spectroscopy. These improvements result in better devices based on the ITO/Ag:NiO x /CH 3 NH 3 PbI 3 /PCBM/BCP/Ag structure with improved average FF (from 69% to 75%), enhanced average J SC (by 1.2 mA/cm 2 absolute) and enhanced average V OC (by 29 mV absolute). The average efficiency of these devices is 16.3% while the best device achieves a PCE of 17.3% with negligible hysteresis and a stabilized efficiency of 17.1%. In comparison, devices that use undoped NiO x have an average efficiency of 13.5%. This work demonstrates that silver is a promising doping material for NiO x by a simple solution process for high-performance inverted PSCs and perovskite tandems.
Source: openalex_inverted_index · Quality: baseline

Research context

OpenAlex topics: Perovskite Materials and Applications · Conducting polymers and applications · Chalcogenide Semiconductor Thin Films

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

Australian Centre for Advanced Photovoltaics, School of Photovoltaic and Renewable Energy Engineering, University of New South Wales, Sydney 2052, Australia

College of Energy, Xiamen University, Xiamen, 361005, China

State Key Laboratory of Silicon Materials, Department of Polymer Science and Engineering, Zhejiang University, Hangzhou 310027, China

Funding

China Scholarship Council · Australian Renewable Energy Agency

References (63)

Show source-provided references
1. 10.1021/acsenergylett.7b0013710.1021/acsenergylett.7b00137 ↗
2. 10.1038/nphoton.2014.13410.1038/nphoton.2014.134 ↗
3. 10.1038/nature1234010.1038/nature12340 ↗
4. 10.1126/science.aan230110.1126/science.aan2301 ↗
5. 10.1021/acsenergylett.7b0057310.1021/acsenergylett.7b00573 ↗
6. 10.1126/science.aah555710.1126/science.aah5557 ↗
7. 10.1038/nmat401410.1038/nmat4014 ↗
8. 10.1126/science.aaa927210.1126/science.aaa9272 ↗
9. 10.1126/science.aaf806010.1126/science.aaf8060 ↗
10. 10.1038/ncomms388510.1038/ncomms3885 ↗
11. 10.1126/science.aah404610.1126/science.aah4046 ↗
12. 10.1016/j.solmat.2016.12.04310.1016/j.solmat.2016.12.043 ↗
13. 10.1021/acsenergylett.6b0069710.1021/acsenergylett.6b00697 ↗
14. 10.1126/science.aad101510.1126/science.aad1015 ↗
15. 10.1039/C6NR02276F10.1039/C6NR02276F ↗
16. 10.1002/aenm.20160045710.1002/aenm.201600457 ↗
17. 10.1002/adma.20160475810.1002/adma.201604758 ↗
18. 10.1039/C5EE00645G10.1039/C5EE00645G ↗
19. 10.1002/anie.20140517610.1002/anie.201405176 ↗
20. 10.1039/C4EE02833C10.1039/C4EE02833C ↗
21. 10.1039/C5TA08193A10.1039/C5TA08193A ↗
22. 10.1021/acs.jpclett.5b0227310.1021/acs.jpclett.5b02273 ↗
23. 10.1038/nphoton.2014.28410.1038/nphoton.2014.284 ↗
24. 10.1039/C5TA05286F10.1039/C5TA05286F ↗
25. 10.1021/acsami.5b0133010.1021/acsami.5b01330 ↗
26. 10.1039/C5TA02265G10.1039/C5TA02265G ↗
27. 10.1021/acsnano.6b0190410.1021/acsnano.6b01904 ↗
28. 10.1039/C7TA02228J10.1039/C7TA02228J ↗
29. 10.1063/1.494141610.1063/1.4941416 ↗
30. 10.1021/acsami.7b0222310.1021/acsami.7b02223 ↗
31. 10.1038/nphoton.2013.34110.1038/nphoton.2013.341 ↗
32. 10.1021/acsnano.5b0704310.1021/acsnano.5b07043 ↗
33. 10.1021/acsnano.5b0813510.1021/acsnano.5b08135 ↗
34. 10.1039/C5TA07957H10.1039/C5TA07957H ↗
35. 10.1007/s12274-016-1181-z10.1007/s12274-016-1181-z ↗
36. 10.1021/acs.jpclett.5b0001010.1021/acs.jpclett.5b00010 ↗
37. 10.1246/cl.15044510.1246/cl.150445 ↗
38. 10.1021/acs.jpcc.5b1154010.1021/acs.jpcc.5b11540 ↗
39. 10.1039/C7NR04692H10.1039/C7NR04692H ↗
40. 10.1021/am403056510.1021/am4030565 ↗
41. 10.1021/acs.nanolett.5b0011610.1021/acs.nanolett.5b00116 ↗
42. 10.1002/ente.20170042210.1002/ente.201700422 ↗
43. 10.1002/aenm.20170168810.1002/aenm.201701688 ↗
44. 10.1021/acsami.6b1597510.1021/acsami.6b15975 ↗
45. 10.1364/OE.24.0A134910.1364/OE.24.0A1349 ↗
46. 10.1039/C6TC03624D10.1039/C6TC03624D ↗
47. 10.1039/C6NR01601D10.1039/C6NR01601D ↗
48. 10.1002/cssc.20170061210.1002/cssc.201700612 ↗
49. 10.1002/adma.20170107310.1002/adma.201701073 ↗
50. 10.1021/ph500006710.1021/ph5000067 ↗
51. 10.1038/nnano.2015.23010.1038/nnano.2015.230 ↗
52. 10.1016/j.nanoen.2016.02.03310.1016/j.nanoen.2016.02.033 ↗
53. 10.1021/acsami.6b1337210.1021/acsami.6b13372 ↗
54. 10.1002/adma.20160469510.1002/adma.201604695 ↗
55. 10.1021/acsnano.6b0242510.1021/acsnano.6b02425 ↗
56. 10.1002/adma.20140418910.1002/adma.201404189 ↗
57. 10.1002/aenm.20170072210.1002/aenm.201700722 ↗
58. 10.1016/j.solmat.2017.04.02910.1016/j.solmat.2017.04.029 ↗
59. 10.1107/S056773947600155110.1107/S0567739476001551 ↗
60. 10.1002/aenm.20130027210.1002/aenm.201300272 ↗
61. 10.1016/j.nanoen.2016.04.06010.1016/j.nanoen.2016.04.060 ↗
62. 10.1016/j.tsf.2011.01.05810.1016/j.tsf.2011.01.058 ↗
63. 10.7567/JJAP.55.02BF0410.7567/JJAP.55.02BF04 ↗