Unveiling the Thickness-Dependent Volumetric Optothermal Energy-Conversion (Self-Heating) Ability of Room Temperature-Grown GaN Thin Films on Direct Amorphous Glass Substrates

Srivathsava Surabhi, Francisco Solis-Pomar, Shiva Samhitha, Abel Fundora, Mitchel A. Ruiz-Robles, Claudio Gutierrez-Lazos, Koduri Ramam, Jong-Ryul Jeong, Manuel Melendrez, Eduardo Perez-Tijerina

Publisher page

Abstract

In this study, we demonstrate an efficient optical-to-thermal energy-conversion (self-heating) ability of room temperature (RT)-grown gallium nitride (GaN) thin films on direct amorphous glass substrates. Radio frequency (rf) magnetron sputtering was employed to experimentally achieve the RT crystallinity of these films directly on glass substrates. Finite-difference time-domain (FDTD) simulations are implemented to elucidate their optothermal response. Our experimental approach precludes the need for conventional prerequisites such as pre- or postannealing, substrate heating, or utilizing buffer (nucleation) nanolayers during the fabrication of GaN thin films on glass substrates. Notably, thin films with an excellent hexagonal wurtzite polymorphic phase comprising mainly (101), (002), and (100) planes is witnessed. Comprehensive characterizations, including structural, morphological, elemental, and surficial analyses, were performed using X-ray diffraction (XRD), scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS), transmission electron microscopy (TEM) with selected area electron diffraction (SAED), and atomic force microscopy (AFM), correspondingly. These analyses confirm the exceptional homogeneity, morphology, and structural integrity of the RT-grown GaN films on the glass. Furthermore, this study also examined the influence of rf-power and gas flow on the film growth rate, thickness, and overall quality. Thickness ( t GaN ) dependent optical response, power absorption ( P abs ), and volumetric power dissipation ( P abs-density ) in the GaN films were analyzed across the ultraviolet–visible (UV–visible) spectrum using FDTD simulations. Our findings offer a potentially transformative approach for the cost-effective, large-scale production of GaN substrates that are crucial for power and optoelectronic applications. This work paves the way for futuristic advancements by facilitating further investigation into critical challenges such as strain-induced crystallographic orientation issues, phase stability, and mitigation of lattice mismatch and dislocation defects in ultrathin GaN films. Furthermore, our research plays a vital role in unlocking the full potential of GaN films in energy harvesting applications.
Source: openalex_inverted_index · Quality: baseline

Research context

OpenAlex topics: GaN-based semiconductor devices and materials · ZnO doping and properties · Ga2O3 and related materials

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

Departamento de Ingeniería de Materiales (DIMAT), Facultad de Ingeniería (FI), Universidad de Concepción (UdeC), 315 Edmundo Larenas, Concepción 4070409, Chile

Laboratorio de Nanociencias y Nanotecnología, Facultad de Ciencias Físico Matemáticas (CICFM-FCFM), Universidad Autónoma de Nuevo León (UANL), San Nicolás de los Garza, Nuevo León, 66451, Mexico

Drug Delivery Laboratory, Departamento de Ciencias y Tecnología Farmacéuticas, Facultad de Ciencias Químicas y Farmacéuticas

Universidad de Chile

Instituto Superior de Tecnologías y Ciencias Aplicadas (InSTEC), Universidad de La Habana, Ave Salvador Allende No. 1110, Quinta de los Molinos, Plaza, La Habana Apartado Postal 6163, Cuba

Department of Materials Science and Engineering, Graduate School of Energy Science and Technology

Chungnam National University

Facultad de Ciencias para el Cuidado de la Salud, Universidad San Sebastían, Campus Las Tres Pascualas, Lientur 1457, Concepción 4060000, Chile

Funding

National Research Foundation of Korea · Fondo Nacional de Desarrollo Cient?fico y Tecnol?gico

References (70)

Show source-provided references
1. 10.1016/j.pcrysgrow.2016.04.01910.1016/j.pcrysgrow.2016.04.019 ↗
2. 10.7567/JJAP.54.03010110.7567/JJAP.54.030101 ↗
3. Rohm Semiconductors. SiC Power Devices and Modules, Application Note 2013, Rev. 001. 2013, https://www.rohm.com/documents/11303/2861707/sic_app-note.pdf (accessed 2025-03-04).
4. 10.1038/srep0532510.1038/srep05325 ↗
5. 10.1143/APEX.4.08210210.1143/APEX.4.082102 ↗
6. 10.1063/1.164080110.1063/1.1640801 ↗
7. 10.4028/www.scientific.net/MSF.971.7910.4028/www.scientific.net/MSF.971.79 ↗
8. 10.1186/s11671-021-03554-710.1186/s11671-021-03554-7 ↗
9. 10.1088/0268-1242/31/3/03400110.1088/0268-1242/31/3/034001 ↗
10. 10.1143/JJAP.35.L7410.1143/JJAP.35.L74 ↗
11. 10.1063/1.9654910.1063/1.96549 ↗
12. 10.1063/1.12077510.1063/1.120775 ↗
13. 10.1063/1.474675110.1063/1.4746751 ↗
14. 10.1021/j150340a01510.1021/j150340a015 ↗
15. 10.1063/1.165284510.1063/1.1652845 ↗
16. 10.1149/1.240785310.1149/1.2407853 ↗
17. 10.1016/0022-0248(72)90175-310.1016/0022-0248(72)90175-3 ↗
18. 10.1016/0022-0248(84)90071-X10.1016/0022-0248(84)90071-X ↗
19. 10.1063/1.11812310.1063/1.118123 ↗
20. 10.1063/1.275312210.1063/1.2753122 ↗
21. 10.1393/ncr/i2018-10154-x10.1393/ncr/i2018-10154-x ↗
22. 10.1063/1.345366010.1063/1.3453660 ↗
23. 10.1116/1.59081810.1116/1.590818 ↗
24. 10.1063/1.36966410.1063/1.369664 ↗
25. 10.1016/S0927-796X(02)00008-610.1016/S0927-796X(02)00008-6 ↗
26. 10.1016/S0921-5107(02)00043-010.1016/S0921-5107(02)00043-0 ↗
27. 10.1016/j.apsusc.2010.03.09710.1016/j.apsusc.2010.03.097 ↗
28. 10.1016/j.microrel.2015.07.01210.1016/j.microrel.2015.07.012 ↗
29. 10.1063/1.482887310.1063/1.4828873 ↗
30. 10.1126/science.281.5379.95610.1126/science.281.5379.956 ↗
31. 10.1103/PhysRevB.65.07531010.1103/PhysRevB.65.075310 ↗
32. 10.1063/1.320231710.1063/1.3202317 ↗
33. 10.3390/cryst1303050010.3390/cryst13030500 ↗
34. 10.1049/el:2004007110.1049/el:20040071 ↗
35. 10.1063/1.346345510.1063/1.3463455 ↗
36. 10.1063/1.35727310.1063/1.357273 ↗
37. 10.1143/JJAP.32.152810.1143/JJAP.32.1528 ↗
38. 10.1063/1.35791610.1063/1.357916 ↗
39. 10.1016/j.tsf.2008.07.03810.1016/j.tsf.2008.07.038 ↗
40. 10.1038/nphoton.2011.25310.1038/nphoton.2011.253 ↗
41. 10.1680/jemmr.19.0001310.1680/jemmr.19.00013 ↗
42. 10.1039/c2jm34405j10.1039/c2jm34405j ↗
43. 10.3390/molecules2723812310.3390/molecules27238123 ↗
44. 10.1088/0022-3727/48/38/38510110.1088/0022-3727/48/38/385101 ↗
45. 10.4236/JMP.2016.71517810.4236/JMP.2016.715178 ↗
46. 10.1007/s41779-019-00420-910.1007/s41779-019-00420-9 ↗
47. 10.1007/s11664-023-10602-810.1007/s11664-023-10602-8 ↗
48. 10.1117/12.50752810.1117/12.507528 ↗
49. 10.1007/s10853-013-7590-410.1007/s10853-013-7590-4 ↗
50. 10.1002/pssa.20120056110.1002/pssa.201200561 ↗
51. 10.1590/1980-5373-MR-2015-045310.1590/1980-5373-MR-2015-0453 ↗
52. 10.1016/j.ceramint.2021.06.03110.1016/j.ceramint.2021.06.031 ↗
53. 10.1088/1361-6633/aa7bb210.1088/1361-6633/aa7bb2 ↗
54. 10.1002/pssa.20120056110.1002/pssa.201200561 ↗
55. 10.1016/S0022-0248(74)80055-210.1016/S0022-0248(74)80055-2 ↗
56. 10.1143/APEX.5.10550210.1143/APEX.5.105502 ↗
57. 10.1063/1.35441410.1063/1.354414 ↗
58. 10.1038/ncomms1050210.1038/ncomms10502 ↗
59. 10.1143/JJAP.30.L206210.1143/JJAP.30.L2062 ↗
60. 10.1063/1.11627410.1063/1.116274 ↗
61. 10.1016/j.jmst.2024.05.03910.1016/j.jmst.2024.05.039 ↗
62. 10.1016/j.tsf.2009.10.14510.1016/j.tsf.2009.10.145 ↗
63. 10.1016/j.arabjc.2015.10.01210.1016/j.arabjc.2015.10.012 ↗
64. 10.1016/j.ceramint.2019.11.02610.1016/j.ceramint.2019.11.026 ↗
65. 10.1063/1.495507610.1063/1.4955076 ↗
66. 10.1103/PhysRevB.51.1332610.1103/PhysRevB.51.13326 ↗
67. 10.1063/1.11776710.1063/1.117767 ↗
68. 10.1103/PhysRevB.58.1257110.1103/PhysRevB.58.12571 ↗
69. 10.1021/es050338z10.1021/es050338z ↗
70. 10.1016/0038-1098(86)90924-510.1016/0038-1098(86)90924-5 ↗