Achieving Face-Selective Ohmic Contact to β-Ga₂O₃ via Anisotropic Trench Structure

High Resolution Image Download MS PowerPoint Slide Achieving low contact resistance is crucial for fabricating high-performance electronic and optoelectronic devices. As beta-gallium oxide (β-Ga 2 O 3 ) with a low-symmetry monoclinic structure exhibits anisotropic electronic properties, we investigated the anisotropic contact resistance of β-Ga 2 O 3 by fabricating trench contact structures on six distinct crystallographic planes ((001), (100), (101), (102), (201), and (−201)) using photo-enhanced metal-assisted chemical etching on undoped (010)-oriented substrates. Trench contact structures enable contacts on distinct crystallographic planes, overcoming the restriction of contact formation to the grown surface. Transfer length method analysis revealed that trench contacts on the (−201) plane yielded the lowest contact resistance (0.23 kΩ·mm). The low atomic density and surface energy enhanced carrier injection at the interface owing to the lower phonon density and formation of a thinner Ti–TiO x interfacial layer, respectively. Asymmetric self-powered ultraviolet–C photodetectors incorporating (−201) trench contacts exhibited superior optoelectronic performance, including a 3-fold increase in responsivity (13.17 mA·W –1 ) with enhanced photo-to-dark current ratio (1.38 × 10 4 %), compared with that of surface-contacted devices (4.38 mA·W –1, 7.57 × 10 3 %). This work highlights the importance of anisotropic properties in contact engineering and provides a pathway for optimizing β-Ga 2 O 3 devices for next-generation power and photodetection technologies.