Highly transparent and conductive indium-doped zinc oxide films deposited at low substrate temperature by spray pyrolysis from water-based solutions
Source abstract
Abstract
In this paper, indium-doped zinc oxide (IZO) films were grown by spray pyrolysis, using zinc acetate and indium acetylacetonate precursors. The focus was on developing a solution recipe based on water as solvent, with only minor acetic acid content, as well as keeping the substrate temperature as low as possible—at 360 °C. The process is therefore environment friendly and energy efficient. Despite the challenging conditions, the resulting IZO films were highly transparent and conductive. Their texture deviates strongly from the (002) texture of ZnO and depends on the indium content, which also influences the resistivity. The latter attains its minimum for an indium concentration of 4 at.% in the solution and decreases for increasing film thickness, reaching the value of (5.0 ± 0.1) × 10−3 Ω cm, mainly due to the increase in carrier mobility. The stability of the resistivity after high dose of UV irradiation was found to increase with the carrier density and the film thickness. Thick, highly doped films show minimal resistivity modification even after a total dose of 12.1 kJ/cm2 UVA/UVB irradiation. Finally, to demonstrate its applicability in devices, the IZO electrode was used for the fabrication of a lead-perovskite absorber solar cell, yielding an energy conversion efficiency of 6% and 910 mV open-circuit voltage.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: ZnO doping and properties · Gas Sensing Nanomaterials and Sensors · Copper-based nanomaterials and applications
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (28)
Show source-provided references
1. Özgür Ü, Alivov YI, Liu C et al (2005) A comprehensive review of ZnO materials and devices. J Appl Phys 98:041301. doi: 10.1063/1.199266610.1063/1.1992666 ↗
2. Ellmer K, Klein A, Rech B (2008) Transparent conductive zinc oxide. Springer, Berlin10.1007/978-3-540-73612-7 ↗
3. Perednis D, Gauckler L (2005) Thin film deposition using spray pyrolysis. J Electroceramics 14:103–111. doi: 10.1007/s10832-005-0870-x10.1007/s10832-005-0870-x ↗
4. Major S, Banerjee A, Chopra KL (1983) Highly transparent and conducting indium-doped zinc oxide films by spray pyrolysis. Thin Solid Films 108:333–340. doi: 10.1016/0040-6090(83)90082-210.1016/0040-6090(83)90082-2 ↗
5. Benouis CE, Benhaliliba M, Sanchez Juarez A et al (2010) The effect of indium doping on structural, electrical conductivity, photoconductivity and density of states properties of ZnO films. J Alloys Compd 490:62–67. doi: 10.1016/j.jallcom.2009.10.09810.1016/j.jallcom.2009.10.098 ↗
6. Yan W, Tan J, Zhang W et al (2012) Tailoring the structure and properties of ZnO: in films by different kinds of acids. Mater Lett 87:28–30. doi: 10.1016/j.matlet.2012.07.06110.1016/j.matlet.2012.07.061 ↗
7. Zaleta-Alejandre E, Camargo-Martinez J, Ramirez-Garibo A et al (2012) Structural, electrical and optical properties of indium chloride doped ZnO films synthesized by Ultrasonic Spray Pyrolysis technique. Thin Solid Films 524:44–49. doi: 10.1016/j.tsf.2012.09.05010.1016/j.tsf.2012.09.050 ↗
8. Castañeda L, Maldonado A, Escobedo-Morales A et al (2011) Indium doped zinc oxide thin films deposited by ultrasonic spray pyrolysis technique: effect of the substrate temperature on the physical properties. Mater Sci Semicond Process 14:114–119. doi: 10.1016/j.mssp.2011.01.01310.1016/j.mssp.2011.01.013 ↗
9. Jiao BC, Zhang XD, Wei CC et al (2011) Effect of acetic acid on ZnO: in transparent conductive oxide prepared by ultrasonic spray pyrolysis. Thin Solid Films 520:1323–1329. doi: 10.1016/j.tsf.2011.04.15210.1016/j.tsf.2011.04.152 ↗
10. Gómez H, Maldonado A, Asomoza R et al (1997) Characterization of indium-doped zinc oxide films deposited by pyrolytic spray with different indium compounds as dopants. Thin Solid Films 293:117–123. doi: 10.1016/S0040-6090(96)09001-310.1016/S0040-6090(96)09001-3 ↗
11. Castañeda L, García-Valenzuela A, Zironi EP et al (2006) Formation of indium-doped zinc oxide thin films using chemical spray techniques: the importance of acetic acid content in the aerosol solution and the substrate temperature for enhancing electrical transport. Thin Solid Films 503:212–218. doi: 10.1016/j.tsf.2005.12.26310.1016/j.tsf.2005.12.263 ↗
12. Biswal R, Maldonado A, Vega-Pérez J et al (2014) Indium Doped Zinc Oxide Thin Films Deposited by Ultrasonic Chemical Spray Technique, Starting from Zinc Acetylacetonate and Indium Chloride. Materials 7:5038–5046. doi: 10.3390/ma707503810.3390/ma7075038 ↗
13. Wienke J, Booij AS (2008) ZnO: in deposition by spray pyrolysis — Influence of the growth conditions on the electrical and optical properties. Thin Solid Films 516:4508–4512. doi: 10.1016/j.tsf.2007.05.07810.1016/j.tsf.2007.05.078 ↗
14. Kriisa M, Krunks M, Kärber E et al (2013) Effect of Solution Spray Rate on the Properties of Chemically Sprayed ZnO. In Thin Films. J Nanomater 2013:1–9. doi: 10.1155/2013/42363210.1155/2013/423632 ↗
15. Vent M, Kärber E, Unt T et al (2012) The effect of growth temperature and spraying rate on the properties of ZnO: in films. Phys Status Solidi C 9:1604–1606. doi: 10.1002/pssc.20120000810.1002/pssc.201200008 ↗
16. Edinger S, Bekacz J, Richter M et al (2015) Influence of the acetic acid concentration on the growth of zinc oxide thin films prepared by spray pyrolysis of aqueous solutions. Thin Solid Films 594(Part B):238–244. doi: 10.1016/j.tsf.2015.04.02710.1016/j.tsf.2015.04.027 ↗
17. Paraguay DF, Estrada LW, Acosta NDR et al (1999) Growth, structure and optical characterization of high quality ZnO thin films obtained by spray pyrolysis. Thin Solid Films 350:192–202. doi: 10.1016/S0040-6090(99)00050-410.1016/S0040-6090(99)00050-4 ↗
18. Wu P, Gao Y-M, Kershaw R et al (1990) Growth and characterization of gallium (III) oxide films. Mater Res Bull 25:357–363. doi: 10.1016/0025-5408(90)90108-E10.1016/0025-5408(90)90108-E ↗
19. Vai AT, Kuznetsov VL, Dilworth JR, Edwards PP (2014) UV-induced improvement in ZnO thin film conductivity: a new in situ approach. J Mater Chem C 2:9643–9652. doi: 10.1039/C4TC01749H10.1039/C4TC01749H ↗
20. Chen S, McLachlan M, Sapelkin A, Binions R (2015) Aerosol assisted chemical vapour deposition of transparent conductive ZnO thin films with hexagonal microplate surfaces and ultrahigh haze values. J Mater Chem A 3:22311–22315. doi: 10.1039/C5TA06029J10.1039/C5TA06029J ↗
21. Patterson AL (1939) The Scherrer Formula for X-Ray Particle Size Determination. Phys Rev 56:978–982. doi: 10.1103/PhysRev.56.97810.1103/PhysRev.56.978 ↗
22. Tauc J (1968) Optical properties and electronic structure of amorphous Ge and Si. Mater Res Bull 3:37–46. doi: 10.1016/0025-5408(68)90023-810.1016/0025-5408(68)90023-8 ↗
23. Sans JA, Sánchez-Royo JF, Segura A et al (2009) Chemical effects on the optical band-gap of heavily doped ZnO: M III (M = Al, Ga, In): An investigation by means of photoelectron spectroscopy, optical measurements under pressure, and band structure calculations. Phys Rev B 79:195105. doi: 10.1103/PhysRevB.79.19510510.1103/PhysRevB.79.195105 ↗
24. Park CH, Zhang SB, Wei S-H (2002) Origin of p-type doping difficulty in ZnO: the impurity perspective. Phys Rev B 66:073202. doi: 10.1103/PhysRevB.66.07320210.1103/PhysRevB.66.073202 ↗
25. Bao J, Shalish I, Su Z et al (2011) Photoinduced oxygen release and persistent photoconductivity in ZnO nanowires. Nanoscale Res Lett 6:404. doi: 10.1186/1556-276X-6-40410.1186/1556-276X-6-404 ↗
26. Morfa AJ, MacDonald BI, Subbiah J, Jasieniak JJ (2014) Understanding the chemical origin of improved thin-film device performance from photodoped ZnO nanoparticles. Sol Energy Mater Sol Cells 124:211–216. doi: 10.1016/j.solmat.2014.02.00210.1016/j.solmat.2014.02.002 ↗
27. Agarwal A, Tomozawa M (1997) Correlation of silica glass properties with the infrared spectra. J Non-Cryst Solids 209:166–174. doi: 10.1016/S0022-3093(96)00542-X10.1016/S0022-3093(96)00542-X ↗
28. Fuchs P, Hagendorfer H, Romanyuk YE, Tiwari AN (2015) Doping strategies for highly conductive Al-doped ZnO films grown from aqueous solution. Phys Status Solidi A 212:51–55. doi: 10.1002/pssa.20143114510.1002/pssa.201431145 ↗