Diffuse Phase Transition in Epitaxial BaTiO3 Thin Films

The thickness dependence of the dielectric properties of epitaxial BaTiO₃ thin films was investigated for thicknesses ranging from 15 to 320 nm. The films were deposited by low-pressure metalorganic chemical vapor deposition on (100) MgO substrates. The relative dielectric permittivity and the loss tangent values decreased with decreasing thickness. High-temperature dielectric measurements showed that with decreasing film thickness, the ferroelectric-to-paraelectric transition temperature decreased, the relative dielectric permittivity decreased, and the phase transition was diffuse. The c/a ratio also decreased with decreasing film thickness. The observed behavior for epitaxial films of BaTiO₃ was attributed to the presence of strain in the films.