Fabrication of ultrathin film capacitors by chemical solution deposition

A facile solution-based processing route using standard spin-coating deposition techniques has been developed for the production of reliable capacitors based on lead lanthanum zirconate titanate (PLZT) with active areas of ⩾1 mm² and dielectric layer thicknesses down to 50 nm. With careful control of the dielectric phase development through improved processing, ultrathin capacitors exhibited slim ferroelectric hysteresis loops and dielectric constants of >1000, similar to those of much thicker films. Thus, it has been demonstrated that chemical solution deposition is a viable route to the production of capacitor films which are as thin as 50 nm but are still macroscopically addressable with specific capacitance values >160 nF/mm².