Core–shell CdS:Ga–ZnTe:Sb p–n nano-heterojunctions: fabrication and optoelectronic characteristics
Source abstract
Abstract
Thermal evaporation was developed to fabricate Ga doped CdS core–Sb doped ZnTe shell p–n nano-heterojunctions, which exhibit obvious sensitivity to 638 nm illumination, with a responsivity and a detectivity of 1.55 × 10 3 A W −1 and 8.7 × 10 13 cm Hz 1/2 W −1 , respectively.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Quantum Dots Synthesis And Properties · Chalcogenide Semiconductor Thin Films · ZnO doping and properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
School of Electronic Science and Applied Physics and Anhui Provincial Key Laboratory of Advanced Materials and Devices
Hefei University of Technology
Hefei
People's Republic of China
Department of Materials Science and Engineering
Funding
China Scholarship Council · National Natural Science Foundation of China
References (45)
Show source-provided references
1. Jie · Nano Today · 2010 · 5 · 31310.1016/j.nantod.2010.06.009 ↗
2. Nie · Small · 2013 · 9 · 287210.1002/smll.201203188 ↗
3. Wang · Science · 2006 · 312 · 5771
4. Soci · Nano Lett. · 2007 · 7 · 100310.1021/nl070111x ↗
5. Wang · J. Mater. Chem. C · 2015 · 3 · 59610.1039/C4TC02297A ↗
6. Debgupta · Nanoscale · 2014 · 6 · 914810.1039/C3NR06917F ↗
7. Hua · Nano Lett. · 2009 · 9 · 11210.1021/nl802636b ↗
8. Tak · J. Mater. Chem. · 2009 · 19 · 594510.1039/b904993b ↗
9. Wu · J. Mater. Chem. · 2011 · 21 · 602010.1039/c0jm03971c ↗
10. Huang · Appl. Surf. Sci. · 2008 · 254 · 591710.1016/j.apsusc.2008.03.150 ↗
11. Shin · J. Mater. Chem. C · 2015 · 3 · 8103
12. Li · Adv. Funct. Mater. · 2014 · 24 · 182110.1002/adfm.201302967 ↗
13. Pal · Nano Lett. · 2012 · 12 · 33110.1021/nl203620f ↗
14. Schmuelling · Nanotechnology · 2014 · 25 · 3510.1088/0957-4484/25/35/355401 ↗
15. Sun · Nanoscale · 2014 · 6 · 656310.1039/C4NR00533C ↗
16. Li · J. Mater. Chem. C · 2014 · 2 · 825210.1039/C4TC01503G ↗
17. Pan · ACS Nano · 2010 · 4 · 67110.1021/nn901699h ↗
18. Kellar · J. Mater. Chem. A · 2013 · 1 · 1242610.1039/c3ta12793a ↗
19. Jie · Appl. Phys. Lett. · 2006 · 89 · 22311710.1063/1.2398891 ↗
20. Wang · J. Appl. Phys. · 2014 · 115 · 06310810.1063/1.4865740 ↗
21. Li · Adv. Energy Mater. · 2013 · 3 · 57910.1002/aenm.201200868 ↗
22. Ye · ACS Appl. Mater. Interfaces · 2010 · 2 · 340610.1021/am1007672 ↗
23. Xiao · Nano Lett. · 2011 · 11 · 112210.1021/nl1040308 ↗
24. Zapien · Appl. Phys. Lett. · 2007 · 90 · 21311410.1063/1.2736286 ↗
25. Xu · Nano Lett. · 2012 · 12 · 500310.1021/nl302693c ↗
26. Ma · Nano Lett. · 2007 · 7 · 330010.1021/nl0715286 ↗
27. Jie · Nano Lett. · 2006 · 6 · 188710.1021/nl060867g ↗
28. Wu · J. Mater. Chem. · 2012 · 22 · 2327210.1039/c2jm34869a ↗
29. Dietl · Science · 2000 · 287 · 101910.1126/science.287.5455.1019 ↗
30. Luo · RSC Adv. · 2015 · 5 · 1332410.1039/C4RA14096F ↗
31. Zhan · Adv. Mater. · 2000 · 12 · 134810.1002/1521-4095(200009)12:18<1348::AID-ADMA1348>3.0.CO;2-X ↗
32. Cao · Opt. Express · 2011 · 19 · 610010.1364/OE.19.006100 ↗
33. Wu · Appl. Phys. Lett. · 2010 · 96 · 12311810.1063/1.3360206 ↗
34. Wu · Nanotechnology · 2010 · 21 · 50520310.1088/0957-4484/21/50/505203 ↗
35. Cai · Phys. Chem. Chem. Phys. · 2011 · 13 · 1466310.1039/c1cp21104h ↗
36. Li · Adv. Mater. · 2010 · 22 · 316110.1002/adma.201000144 ↗
37. Ehsan · RSC Adv. · 2015 · 5 · 618610.1039/C4RA13593H ↗
38. Wang · Nanoscale · 2014 · 6 · 367910.1039/C3NR06137J ↗
39. Tobin · J. Electron. Mater. · 1995 · 24 · 69710.1007/BF02657981 ↗
40. Wang · Part. Part. Syst. Charact. · 2013 · 30 · 63010.1002/ppsc.201300040 ↗
41. Zeng · ACS Appl. Mater. Interfaces · 2013 · 5 · 936210.1021/am4026505 ↗
42. Amos · J. Am. Chem. Soc. · 2007 · 129 · 1429610.1021/ja073675b ↗
43. He · J. Mater. Sci. · 2014 · 25 · 1499
44. Manna · J. Phys. Chem. C · 2012 · 116 · 712610.1021/jp210455w ↗
45. Lee · Nat. Nanotechnol. · 2011 · 6 · 34810.1038/nnano.2011.46 ↗