Cross-linkable random copolymers as dielectrics for low-voltage organic field-effect transistors
Source abstract
Abstract
A novel co- and terpolymer utilizing cross-linkable azide groups has been proven to be applicable as thin-film dielectric in organic field effect transistors. Reliable operation with saturation currents above V g = 4 to 5 V can be achieved for a dielectric thickness of smaller than 100 nm.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Organic Electronics and Photovoltaics · Semiconductor materials and devices · Molecular Junctions and Nanostructures
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Materials Science and Geoscience
Technische Universität Darmstadt
64287 Darmstadt
Germany
Fraunhofer Institute for Applied Polymer Research
14476 Potsdam-Golm
Funding
Helmholtz Association · Deutsche Forschungsgemeinschaft
References (39)
Show source-provided references
1. Veres · Chem. Mater. · 2004 · 16 · 454310.1021/cm049598q ↗
2. Facchetti · Adv. Mater. · 2005 · 17 · 170510.1002/adma.200500517 ↗
3. Yoon · J. Am. Chem. Soc. · 2006 · 128 · 1285110.1021/ja063290d ↗
4. Ortiz · Chem. Rev. · 2010 · 110 · 20510.1021/cr9001275 ↗
5. Halik · Nature · 2004 · 431 · 96310.1038/nature02987 ↗
6. Huang · Org. Electron. · 2010 · 11 · 61810.1016/j.orgel.2010.01.001 ↗
7. Yun · J. Appl. Phys. · 2009 · 105 · 03450810.1063/1.3075616 ↗
8. Chua · Appl. Phys. Lett. · 2004 · 84 · 340010.1063/1.1710716 ↗
9. Zan · IEEE Electron Device Lett. · 2011 · 32 · 113110.1109/LED.2011.2155026 ↗
10. Jo · Macromol. Res. · 2010 · 18 · 77710.1007/s13233-010-0805-5 ↗
11. Meena · RSC Adv. · 2014 · 4 · 1849310.1039/C4RA01517G ↗
12. Roberts · Chem. Mater. · 2009 · 21 · 229210.1021/cm900637p ↗
13. Wang · Chem. Mater. · 2013 · 25 · 480610.1021/cm403203k ↗
14. Xu · Org. Electron. · 2010 · 11 · 83610.1016/j.orgel.2010.01.026 ↗
15. Vicca · Thin Solid Films · 2010 · 519 · 39110.1016/j.tsf.2010.08.009 ↗
16. Yoon · J. Am. Chem. Soc. · 2005 · 127 · 1038810.1021/ja052488f ↗
17. Wang · Jpn. J. Appl. Phys. · 2012 · 51 · 09MJ0210.7567/JJAP.51.09MJ02 ↗
18. Hwang · Appl. Phys. Lett. · 2006 · 89 · 09350710.1063/1.2345243 ↗
19. Lim · Appl. Phys. Lett. · 2007 · 90 · 17351210.1063/1.2733626 ↗
20. Pyo · J. Mater. Res. · 2005 · 20 · 93110.1557/JMR.2005.0121 ↗
21. Loffredo · J. Disp. Technol. · 2015 · 11 · 53310.1109/JDT.2014.2363685 ↗
22. Jang · ACS Appl. Mater. Interfaces · 2015 · 7 · 527410.1021/am508573q ↗
23. Xu · Org. Electron. · 2015 · 12 · 204010.1016/j.orgel.2011.08.029 ↗
24. Xu · Org. Electron. · 2010 · 11 · 83610.1016/j.orgel.2010.01.026 ↗
25. Kim · J. Polym. Sci., Part A: Polym. Chem. · 2008 · 46 · 171010.1002/pola.22512 ↗
26. Li · J. Mater. Chem. C · 2014 · 2 · 351710.1039/c4tc00116h ↗
27. Spruell · J. Am. Chem. Soc. · 2011 · 133 · 1669810.1021/ja207635f ↗
28. Bräse · Angew. Chem., Int. Ed. · 2005 · 44 · 518810.1002/anie.200400657 ↗
29. Pötzsch · Macromol. Rapid Commun. · 2012 · 33 · 63510.1002/marc.201100795 ↗
30. Steppan · Angew. Chem., Int. Ed. · 1982 · 21 · 45510.1002/anie.198204553 ↗
31. Bang · Adv. Mater. · 2007 · 19 · 455210.1002/adma.200701866 ↗
32. Wang · Appl. Phys. Lett. · 2012 · 101 · 03330310.1063/1.4737173 ↗
33. Ma · Adv. Funct. Mater. · 2010 · 20 · 137110.1002/adfm.200902236 ↗
34. Benson · Phys. Status Solidi · 2008 · 205 · 47510.1002/pssa.200723421 ↗
35. Kehrer · Synth. Methods · 2012 · 161 · 255810.1016/j.synthmet.2011.08.007 ↗
36. Torres · Appl. Phys. Lett. · 2004 · 85 · 31410.1063/1.1769081 ↗
37. Watson · Appl. Phys. Lett. · 2011 · 99 · 22330410.1063/1.3665190 ↗
38. Estrada · Solid-State Electron. · 2008 · 52 · 5310.1016/j.sse.2007.07.007 ↗
39. Günther · Appl. Phys. Lett. · 2015 · 106 · 23330110.1063/1.4922422 ↗