Pseudo-high-entropy engineering via multi-valence states enables thermodynamically favorable CO 2 activation in perovskite–rGO heterojunctions
Source abstract
Abstract
Multi-valence Mn substitution (Mn 2+ /Mn 3+ /Mn 4+ ) in SrTiO 3 integrated with 2D rGO creates a pseudo-high-entropy state, breaking local centrosymmetry and generating Ti 3+ shallow traps and oxygen vacancies for noble-metal-free CO 2 reduction.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Advancements in Solid Oxide Fuel Cells · CO2 Reduction Techniques and Catalysts · Electrocatalysts for Energy Conversion
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Department of Chemistry, College of Natural Sciences, Yeungnam University, Gyeongbuk 38541, Gyeongsan, Republic of Korea
School of Bioengineering and Food Technology, Faculty of Applied Sciences and Biotechnology, Shoolini University, Solan, Himachal Pradesh 173229, India
Funding
National Research Foundation of Korea · Ministry of Science and ICT, South Korea
References (60)
Show source-provided references
1. Albert · World Gov. · 2021 · 46 · 11040610.1177/030437542110406 ↗
2. Zhang · SmartMat · 2022 · 3 · 41710.1002/smm2.1095 ↗
3. RaeisianAsl · Mater. Today Sustain. · 2025 · 29 · 10107210.1016/j.mtsust.2025.101072 ↗
4. Chen · Chem. Rev. · 2007 · 107 · 289110.1021/cr0500535 ↗
5. Cai · Adv. Mater. · 2024 · 36 · 240994910.1002/adma.202409949 ↗
6. Sen · ACS Energy Lett. · 2024 · 9 · 369410.1021/acsenergylett.4c01129 ↗
7. Coduri · Small · 2025 · 21 · 240663410.1002/smll.202406634 ↗
8. Yang · Small · 2025 · 21 · e0848110.1002/smll.202508481 ↗
9. Mitra · J. Phys. Chem. C · 2025 · 129 · 1944010.1021/acs.jpcc.5c04697 ↗
10. Ma · J. Mater. Chem. A · 202610.1039/D6TA01678B ↗
11. Uddin · J. Mater. Chem. A · 2026 · 14 · 2278310.1039/D6TA01435F ↗
12. Hidalgo-Jiménez · Acta Mater. · 2026 · 302 · 12163210.1016/j.actamat.2025.121632 ↗
13. Wu · Catalysts · 2025 · 15 · 60710.3390/catal15070607 ↗
14. Thompson · J. Phys. Chem. B · 2003 · 107 · 1170010.1021/jp030430m ↗
15. Set · Appl. Phys. Lett. · 2015 · 107 · 17330110.1063/1.4934920 ↗
16. Moon · Nano Today · 2023 · 49 · 10178510.1016/j.nantod.2023.101785 ↗
17. Darriba · Phys. Rev. B · 2023 · 108 · 24514410.1103/PhysRevB.108.245144 ↗
18. Simenas · Chem. Rev. · 2024 · 124 · 228110.1021/acs.chemrev.3c00532 ↗
19. Liu · ACS Energy Lett. · 2021 · 6 · 252610.1021/acsenergylett.1c00794 ↗
20. Zhang · Acta Mater. · 2024 · 281 · 12041510.1016/j.actamat.2024.120415 ↗
21. Li · Appl. Catal. B Environ. · 2022 · 306 · 12114210.1016/j.apcatb.2022.121142 ↗
22. Youn · Appl. Catal. B Environ. Energy · 2026 · 384 · 12615210.1016/j.apcatb.2025.126152 ↗
23. Kumar · ACS Appl. Energy Mater. · 2025 · 8 · 1347610.1021/acsaem.5c01856 ↗
24. Chu · ACS Appl. Electron. Mater. · 2025 · 7 · 304110.1021/acsaelm.5c00212 ↗
25. Chapron · J. Appl. Phys. · 2019 · 126 · 15410110.1063/1.5115106 ↗
26. Goh · Adv. Sci. · 2025 · 12 · e20250613310.1002/advs.202506133 ↗
27. Chen · Nat. Commun. · 2025 · 16 · 738310.1038/s41467-025-62729-3 ↗
28. Wang · ACS Appl. Mater. Interfaces · 2025 · 17 · 2116810.1021/acsami.4c21690 ↗
29. Amer · RSC Adv. · 2017 · 7 · 82610.1039/C6RA24815B ↗
30. Panicker · Chem. Eng. J. · 2023 · 463 · 14237610.1016/j.cej.2023.142376 ↗
31. Hou · Nat. Commun. · 2021 · 12 · 591710.1038/s41467-021-26160-8 ↗
32. Wang · Chem. Eng. J. · 2025 · 522 · 16759110.1016/j.cej.2025.167591 ↗
33. Park · Nat. Energy · 2025 · 10 · 121510.1038/s41560-025-01852-3 ↗
34. Wang · J. Eur. Ceram. Soc. · 2024 · 44 · 11670910.1016/j.jeurceramsoc.2024.116709 ↗
35. Minitha · ACS Omega · 2018 · 3 · 410510.1021/acsomega.7b02085 ↗
36. Kumar · Vacuum · 2025 · 242 · 11474910.1016/j.vacuum.2025.114749 ↗
37. Zhang · Energy Environ. Sci. · 2024 · 17 · 334710.1039/D4EE00214H ↗
38. Chen · Green Energy Environ. · 2025 · 10 · 134810.1016/j.gee.2025.01.006 ↗
39. Chen · RSC Adv. · 2023 · 13 · 1505510.1039/D3RA01429K ↗
40. Mondal · ACS Omega · 2021 · 6 · 873410.1021/acsomega.0c06045 ↗
41. Wen · ACS Catal. · 2023 · 13 · 1273010.1021/acscatal.3c02932 ↗
42. Nemani · Commun. Mater. · 2023 · 4 · 1610.1038/s43246-023-00341-y ↗
43. Xu · Org. Electron. · 2020 · 81 · 10566310.1016/j.orgel.2020.105663 ↗
44. Othman · Polymers · 2020 · 12 · 211710.3390/polym12092117 ↗
45. Liao · Precis. Chem. · 2024 · 2 · 4910.1021/prechem.3c00112 ↗
46. Saravanan · Catalysts · 2024 · 14 · 41010.3390/catal14070410 ↗
47. Kim · J. Asian Ceram. Soc. · 2021 · 16 · 393710.1002/asia.202101013 ↗
48. Yang · RSC Adv. · 2026 · 16 · 1376510.1039/d6ra00068a ↗
49. Vasiliadou · Interface Focus · 2019 · 9 · 2019007310.1098/rsfs.2019.0073 ↗
50. Sahadevan · Mater. Sci. Eng. B · 2022 · 284 · 11587510.1016/j.mseb.2022.115875 ↗
51. Liu · J. Colloid Interface Sci. · 2025 · 700 · 13834910.1016/j.jcis.2025.138349 ↗
52. Lei · J. Mater. Chem. A · 2025 · 13 · 1271210.1039/D4TA08554J ↗
53. Gao · ACS Catal. · 2024 · 14 · 1074610.1021/acscatal.4c02793 ↗
54. Mariano · PRX Energy · 2024 · 3 · 03300510.1103/PRXEnergy.3.033005 ↗
55. Li · Molecules · 2024 · 29 · 399510.3390/molecules29173995 ↗
56. Zhai · Nat. Photonics · 2026 · 20 · 6310.1038/s41566-025-01800-3 ↗
57. Wang · Langmuir · 2025 · 41 · 1555310.1021/acs.langmuir.5c01687 ↗
58. Madonia · Materials · 2024 · 17 · 231910.3390/ma17102319 ↗
59. Zhou · Fuel · 2026 · 405 · 13666410.1016/j.fuel.2025.136664 ↗
60. Zhang · J. Am. Chem. Soc. · 2023 · 145 · 576910.1021/jacs.2c12632 ↗