Tuning of superconducting phase transition and magnetic properties of ferroelectric-superconducting PbZr0.48Ti0.52O3/YBa2Cu3O7-δ heterostructure

Abstract Tuning of superconducting phase transition temperature (Ts) and interfacial magnetism is of great technological importance for micro and nanoelectronics. To achieve the cherished goal, an ultra-thin layer (4 nm, 6 nm, 8 nm 10 nm) of ferroelectrics PbZr0.48Ti0.52O3 (PZT) on high-temperature superconductor YBa2Cu3O7-δ (YBCO) has deposited to tailor the magnetic and superconducting properties. The existence of Meissner effect confirmed the superconducting nature of YBCO in the heterostructures. However, its Ts significantly shifted to the lower temperature side with an increase in PZT capping layers' thickness. Nearly 10 K reduction in Ts was observed with an increase in the capping layer from 4 to 10 nm. A significant amount of magnetic moment was found in the heterostructures, which increases almost three times compared to the YBCO/LAO magnetic moment above Ts. We believe novel weak magnetic phases above the Ts may be due to the re-arrangement of oxygen anion near the ferroelectric-superconducting interface.