Annealing temperature dependence on the positive bias stability of IGZO thin-film transistors

AbstractThe threshold voltage shift (Δ Vth) under positive-voltage bias stress (PBS) of InGaZnO (IGZO) thin-film transistors (TFTs) annealed at different temperatures in air was investigated. The dramatic degradation of the electrical performance was observed at the sample that was annealed at 700°C. The degradation of the saturation mobility (μsat) resulted from the diffusion of indium atoms into the interface of the IGZO/gate insulator after crystallization, and the degradation of the subthreshold slope (S-factor) was due to the increase in the interfacial and bulk trap density. In spite of the degradation of the electrical performance of the sample that was annealed at 700°C, it showed a smaller Δ Vth under PBS conditions for 104 s than the samples that were annealed at 500°C, which is attributed to the nanocrystal-embedded structure. The sample that was annealed at 600°C showed the best performance and the smallest Δ Vth among the fabricated samples with a μsat of 9.38 cm2/V s, an S-factor of 0.46 V/decade, and a Δ Vth of 0.009 V, which is due to the passivation of the defects by high thermal annealing without structural change.